Urban municipal water supply is an important part of underground pipelines, and their scale continues to expand. Due to the continuous improvement in the quality and quantity of data available for pipeline systems in recent years, traditional pipeline network risk assessment cannot cope with the improvement of various monitoring methods. Therefore, this paper proposes a machine learning-based risk assessment method for municipal pipe network operation and maintenance and builds a model example based on the data of a pipeline network base in a park in Suzhou. We optimized the random forest learning model, compared it with other centralized learning methods, and finally evaluated the model’s learning effect. Finally, the risk probability associated with each pipe segment sample was obtained, the risk factors affecting the pipe segment’s failure were determined, and their relevance and importance ranking was established. The results showed that the most influential factors are pipe material, soil properties, service life, and the number of past failures. The random forest algorithm demonstrated better prediction accuracy and robustness on the dataset.

Adding fibers into cement to form fiber-reinforced soil cement material can effectively enhance its physical and mechanical properties. In order to investigate the effect of fiber type and dosage on the strength of fiber-reinforced soil cement, polypropylene fibers (PPFs), polyvinyl alcohol fibers (PVAFs), and glass fibers (GFs) were blended according to the mass fraction of the mixture of cement and dry soil (0.5%, 1%, 1.5%, and 2%). Unconfined compressive strength tests, split tensile strength tests, scanning electron microscopy (SEM) tests, and mercury intrusion porosimetry (MIP) pore structure analysis tests were conducted. The results indicated that the unconfined compressive strength of the three types of fiber-reinforced soil cement peaked at a fiber dosage of 0.5%, registering 26.72 MPa, 27.49 MPa, and 27.67 MPa, respectively. The split tensile strength of all three fiber-reinforced soil cement variants reached their maximum at a 1.5% fiber dosage, recording 2.29 MPa, 2.34 MPa, and 2.27 MPa, respectively. The predominant pore sizes in all three fiber-reinforced soil cement specimens ranged from 10 nm to 100 nm. Furthermore, analysis from the perspective of energy evolution revealed that a moderate fiber dosage can minimize energy loss. This paper demonstrates that the unconfined compressive strength test, split tensile strength test, scanning electron microscopy (SEM), and mercury intrusion porosimetry (MIP) pore structure analysis offer theoretical underpinnings for the utilization of fiber-reinforced soil cement in helical pile core stiffening and broader engineering applications.