Systematic investigations of hardened cement paste, high‐performance concrete and mortar with and without microfibers, subjected to static and cyclic tensile loadings, were conducted. The material degradation was investigated by means of microscopic analyses of the microcrack development. Notched specimens were subjected to a predefined number of load cycles. A nonsteady increase of microcracking with increasing load cycles was observed in high‐strength concrete, whereas the addition of steel fibers lead to a steady increase of microcracks. High‐strength mortar often showed premature failure, while addition of steel micro fibers allowed completion of the cyclic tests. To obtain a deeper insight into physical mechanisms governing fatigue and structural failure, high‐performance concrete (HPC) and fiber‐reinforced concrete (FRC) under static and cyclic tensile loadings have been modeled using cohesive interface finite elements, micromechanics, and a fiber‐bundle model. Analysis of model predictions shows the significance of strength disorder and fiber properties on the structural behavior.

In the present study, the capability of high-strength short steel fibers to control the degradation in high-performance concrete was experimentally examined and numerically simulated. To this end, notched prismatic high-performance concrete specimens with (HPSFRC) and without (HPC) short steel fibers were subjected to static and cyclic tensile tests up to 100,000 cycles. The cyclic tests showed that the rate of strain increase was lower for HPSFRC specimens and that the strain stagnated after around 10,000 cycles, which was not the case with HPC specimens. The microscopic examinations showed that in HPSFRC, a larger number of microcracks developed, but they had a smaller total surface area than the microcracks in the HPC. To further investigate the influence of fibers on the behavior of HPSFRC in the cracked state, displacement-controlled crack opening tests, as well as numerical simulations thereof, were carried out. Experiments have shown, and the numerical simulations have confirmed, that the inclusion of short steel fibers did not significantly affect the ultimate strength; however, it notably increased the post-cracking ductility of the material. Finally, the unloading/reloading behavior was examined, and it was observed that the unloading stiffness was stable even for significant crack openings; however, the hysteresis loops due to unloading/reloading were very small.

There is an increasing need for the development of novel technologies for tunnel construction in difficult geological conditions to protect segmental linings from unexpected large deformations. In the context of mechanized tunneling, one method to increase the damage tolerance of tunnel linings in such conditions is the integration of a compressible two-component grout for the annular gap between the segmental linings and the deformable ground. In this regard, expanded polystyrene (EPS) lightweight concrete/mortar has received increasing interest as a potential “candidate material” for the aforementioned application. In particular, the behavior of the EPS lightweight composites can be customized by modifying their pore structure to accommodate deformations due to specific geological conditions such as squeezing rocks. To this end, novel compressible cementitious EPS-based composite materials with high compaction potential have been developed. Specimens prepared from these composites have been subjected to compressive loads with and without lateral confinement. Based on these experimental data a computational model based on the Discrete Element Method (DEM) has been calibrated and validated. The proposed calibration procedure allows for modeling and prognosis of a wide variety of composite materials with a high compaction potential. The calibration procedure is characterized by the identification of physically quantifiable parameters and the use of phenomenological submodels. Model prognoses show excellent agreement with new experimental measurements that were not incorporated in the calibration procedure.