We have conducted an experimental and theoretical study on first- and second-order Raman scattering of zinc blende and wurtzite ZnS. Based on the calculated phonon band structure, phonon density of states, and symmetry selection rules, we have clearly identified for the first time the origins of these vibration modes in the second-order Raman spectra from these two polymorphs. For zinc blende ZnS, it is found that the previously estimated frequency of the LA mode at X point in the Brillouin-zone boundary is much smaller than the value obtained from other experiments and our calculation. Considering the involvement of LA phonon at X point, we reassign the second-order Raman active modes and some other modes which have not yet been understood so far. This work clarifies some of the controversial Raman mode assignments in zinc blende and wurtzite ZnS.

Hydrogen evolution reaction (HER) has a dominant function in energy conversion and storage because it supplies a most effective way for converting electricity into sustainable high-purity hydrogen. Layered double hydroxides (LDHs) have shown promising performance in the process of electrochemical water oxidation (a half-reaction for water splitting). Nevertheless, HER properties have not been well released due to the structural characteristics of related materials. Herein, a simple and scalable tactics is developed to synthesize chromium-doped CoFe LDH (CoFeCr LDH). Thanks to oxygen vacancy, optimized electronic structure and interconnected array hierarchical structure, our developed ternary CoFeCr-based layered double hydroxide catalysts can provide 10 mA cm⁻² current density at −0.201 V vs. RHE with superior long-term stability in alkaline electrolyte. We anticipate that the simple but feasible polymetallic electronic modulation strategy can strengthen the electrocatalytic property of the layered double hydroxides established in the present study, based on a carbon neutral and hydrogen economy.

ZnO-SnO2 hollow spheres were successfully synthesized through a hydrothermal method-combined carbon sphere template. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy (FT-IR). The average diameter of hollow spheres is about 150 nm. The photocatalytic activity of the as-prepared samples was investigated by photodegrading Rhodamine B. The results indicated that the photocatalytic activities of ZnO-SnO2 hollow spheres are higher than ZnO hollow spheres. The degradation efficiency of the hollow spheres could reach 99.85% within 40 min, while the ZnO hollow spheres need 50 min.

The $\mathrm{Co}∕\mathrm{Zn}\mathrm{O}$ core/shell nanoparticles-filled polymer poly(vinylidene fluoride) (PVDF)-based composites (0-3 connectivity) are fabricated, in which the core/shell structure for preventing Co particles from agglomeration is prepared by a simple wet chemistry procedure. At the same time, the $N,N$ -di(phosphonomethyl)iminoacetic acid (DPMIAA) is used to modify the core/shell surface. High dielectric permittivity and low leakage current are achieved for the DPMIAA-modified $\mathrm{Co}∕\mathrm{Zn}\mathrm{O}$ core/shell nanoparticle-PVDF composite, which shows good homogeneity, no cracks, and fine mechanical flexibility.