The mechanical properties of 3D-printed mortars are determined in terms of their compressive and direct tensile bond strengths. To determine such properties using existing methods, a preliminary experiment was conducted. The compressive strength of the printed mortar was compared to mold-casted specimens and it was found that the compressive strength decreased by ~30%. Among the fabrication variables, an increase in nozzle height negatively influenced the direct tensile bond strength. For the same conditions and age, the direct tensile strength decreased by as much as 16–29% when the number of layers increased from 2 to 6. When the specimens were fabricated using a specially designed stainless steel frame and core drill, followed by extraction and the application of physical impact, the 28 days compressive strength of the specimen decreased by ~50%.

Research and technological advancements in 3D concrete printing (3DCP) have led to the idea of applying it to offshore construction. The effect of gravity is reduced underwater, which can have a positive effect on 3DCP. For basic verification of this idea, this study printed and additively manufactured specimens with the same mortar mixture in air and underwater and evaluated properties in the fresh state and the hardened state. The mechanical properties were evaluated using the specimens produced by direct casting to the mold and specimens produced by extracting from the additive part through coring and cutting. The results of the experiment show that underwater 3D printing required a greater amount of printing output than in-air 3D printing for a good print quality, and buildability was improved underwater compared to that in air. In the case of the specimen layered underwater, the density and compressive strength decreased compared to the specimen layered in air. Because there are almost no effects of moisture evaporation and bleeding in water, the interlayer bond strength of the specimen printed underwater was somewhat larger than that printed in air, while there was no effect of the deposition time interval underwater.

Three-dimensional concrete printing (3DCP) materials require a relatively low water-to-binder ratio (W/B) of 0.3 or less to ensure their buildability and flow properties are sufficiently maintained after mixing. In this study, the rheological properties of 3DCP materials with W/B 0.28 were evaluated up to 60 min after mixing, and the yield stress and plastic viscosity were analyzed over time. A gradual decrease in flow rate with time was observed during the transport of 200 kg of material per batch through a 20 m hose. To examine the time-dependent changes in flow rate and layer volume, a 2200 mm × 1000 mm test specimen was printed. The dependence of the layer width over time during the printing process was measured and analyzed. The experimental analyses showed that the flow rate and layer volume of the 3DCP material gradually decreased with time after mixing, which was correlated with the rheological properties.

This study developed a 3D concrete printing (3DCP) system that can print not only in air but also underwater. This underwater 3DCP system is equipped with many distinct technologies, such as a technology to supply the printing material to the nozzle tip at a constant rate by detecting its amount in the printer hopper. Using the developed 3DCP system, the effect of nozzle details on underwater print quality and hardened properties was investigated. The straight-line printing performance underwater was evaluated using five nozzles: a nozzle without a trowel (Nozzel#1), a nozzle with fixed trowels attached to both sides (Nozzle#2), a nozzle with trowels attached to the back and both sides to constrain five sides (Nozzle#3), a nozzle with a three-sided trowel inclined by 30° (Nozzle#4), and a nozzle with a roof added to Nozzle#4 opening (Nozzle#5). Nozzle#4 yielded the best print quality and hardened properties. In addition, an underwater curved shape printing test was performed using Nozzle#4, the problems that occurred in this test were analyzed and solutions were suggested.