Introduction: Prosthetic joint infections (PJIs) are difficult to treat and represent a significant burden to the healthcare system. Two-stage revision surgery with placement of an antibiotic-loaded cement spacer is currently the gold standard for treatment in the United States for late-onset infections. We evaluate the efficacy of varying doses of vancomycin added to antibiotic-containing acrylic cement spacers and discuss the biomechanical and antimicrobial properties of using high versus low doses of vancomycin in cement spacers in the hip and knee. Materials and Methods: Commercially available Copal cement containing either gentamicin and clindamycin (G + C) or gentamicin and vancomycin (G + V) was prepared with the manual addition of low (2 g) and high (6 g) doses of vancomycin. In vitro mechanical testing was then carried out according to ISO 5833 and DIN 53435, as well as inhibition zone assays against common PJI pathogens. Additionally, inhibition zone assays were conducted on two commercially available prefabricated spacers containing gentamicin: Copal Exchange G and Cemex Spacer-K. Results: In biomechanical testing, Copal G + V with the addition of 6 g of vancomycin failed to meet the ISO standard. Copal G + C and Copal G + V with low and high dosages of vancomycin were all effective against the tested pathogens and displayed constant efficacy for a duration of 42 days. High doses of vancomycin showed significantly lower mechanical stability. Moreover, Copal Exchange G showed significantly larger inhibition zones across 42 days. Discussion: While higher concentrations of vancomycin appear to improve the antimicrobial efficacy of cement, they also reduce its mechanical stability. Despite its smoother surface, the Copal Exchange G spacer exhibits large inhibition zones after 1 day and maintains consistently large inhibition zones over 6 weeks. Thus, it may be preferred for use in two-stage revision surgery. Conclusion: Copal Exchange G is more effective than Cemex Spacer K against S. aureus and E. coli. The manual addition of vancomycin to cement containing double antibiotics is very effective. The influence on ISO compression is low, the ISO bending modulus is increased, and ISO bending, DIN bending, and DIN impact, are reduced.

Background: The number of periprosthetic joint infections caused by vancomycin-resistant pathogens is increasing. Currently, no PMMA cement is commercially available to cover VRE. Daptomycin shows promising results in treating infection, offering a good safety profile and a reduced risk of developing resistance. The purpose of this in vitro study was to investigate the mechanical stability, handling properties, elution behavior, and antimicrobial effectiveness of PMMA cement loaded with three different daptomycin concentrations in comparison to commercially available antibiotic-loaded bone cement (ALBC). Methods: Mechanical properties and handling characteristics (ISO 5833, DIN 53435), HPLC elution, antimicrobial effectiveness with proliferation assay (DIN 17025), and inhibition zone testing were investigated. Results: All tested daptomycin concentrations met the ISO and DIN standards for mechanical strength. Loading of 40 g of PMMA cement with 0.5 g of daptomycin did not show any antimicrobial effectiveness, in contrast to 1.0 g and 1.5 g. PMMA cement with 1.5 g of daptomycin was the best in terms of elution and effectiveness, and it showed good ISO mechanical strength; ISO doughing was sticky for a little longer and setting was faster compared to the vancomycin-containing reference cement. Conclusion: PMMA cement containing 0.5 g of gentamicin and 1.5 g of daptomycin could be a good alternative to the already established COPAL^® (Wehrheim, Germany) G+V for the treatment of PJIs caused by VRE.

Background: Number of joint infections caused by Vancomycin-resistant pathogens is emerging. Currently no PMMA cement is commercially available to cover VRE. Daptomycin shows promising results in infection treatment, offers a good safety profile and reduced risk for resistance development. Purpose of this in vitro study is to investigate the mechanical stability, handling properties, elution behavior and antimicrobial effectiveness of PMMA cement loaded with three different Daptomycin concentrations in comparison to commercially available ALBC; Methods: Mechanical properties and handling characteristics (ISO 5833, DIN 53435), HPLC elution, antimicrobial effectiveness with proliferation assay (DIN 17025) and inhibition zone testing were investigated; Results: All tested Daptomycin concentrations fulfilled ISO and DIN mechanical strength. Dosage of 0.5. g added Daptomycin did not show any antimicrobial effectiveness in contrast to 1.0 g and1.5 g. Cement with 1.5 g Daptomycin was best in elution and effectiveness, showed good mechanical ISO strength, ISO doughing was a little longer sticky and setting was faster as Vancomycin containing reference cement; Conclusion: PMMA cement containing 0.5 g Gentamicin and 1.5 g Daptomycin could be a good alternative to the already established COPAL® G+V for PJI treatment of VRE.

Antibiotic carrier particles of variable size might influence mechanic properties within impacted thermodisinfected and native cancellous bone different. Herafill®G containing calciumsulfate and calciumcarbonate provides high local concentrations of gentamicin being important for revision surgery in infected joint replacements. Native and thermodisinfected cancellous bone derived from 6 to 7 months old piglets was used for in vitro impaction bone grafting and supplemented each with Herafill®G granules of two different sizes. Micromovement of implants related to shear force was measured in 29 specimens distributed in 6 groups. Thermodisinfected cancellous bone revealed a significant higher shear force resistance than native bone with a mean difference of 423.8 mdeg/Nm (p < 0.001) ranging within 95% confidence interval from 181.5 to 666.0 mdeg/Nm. Adding small granules to thermodisinfected bone did not reduce shear force resistance significantly since adding large granules to native bone improved it by 344.0 mdeg/Nm (p < 0.003). Shear force resistance was found higher at the distal region of the implant compared to a proximal point of measurement throughout all specimens. Less impaction impulses were necessary for thermodisinfected bone. Thermodisinfected cancellous bone might achieve a higher degree of impaction compared with native bone resulting in increased resistance against shear force since impaction was found increased distally. Supplementation of thermodisinfected bone with small granules of Herafill®G might be considered for application of local antibiotics. Large granules appeared more beneficial for supplementation of native bone. Heterogeneity of bone graft and technical aspects of the impaction procedure have to be considered regarding the reproducibility of femoral impaction bone grafting.