This study conducts a scientometric review on the use of geopolymer mortar and composites in different construction applications. It aims to analyze the findings of past research and reveal the research constituents, development trends, and knowledge gaps. The Scopus database was employed to retrieve the relevant publications, while Bibliometrix was used to conduct the statistical analyses. Results revealed a steady and gradual increase in the number of publications after 2013, as the annual growth rate increased from 23.9% to 45.2% between the timeframes 2003–2013 and 2014–2022, respectively. The analysis highlighted that many authors collaborated on different construction applications of geopolymers regardless of geographic location. Meanwhile, Construction and Building Materials, China, and Universiti Malaysia Perlis were found to be the predominant journal, country, and institution, respectively. The scientometric analysis showed that the most frequently investigated applications for geopolymer mortars and composites were fire resistance, corrosion protection, and repair. Research gaps highlighted that other applications are not as well investigated despite the promising performance of the geopolymer composites, including 3D printing, heavy metals absorption, environmental protection, and underwater applications. Future research is required to assess the use of other alumina and silica-rich binders in geopolymers while also exploring their lifecycle assessment and economic impact.

This study investigates the effect of accelerated carbonation curing on the carbon sequestration potential, performance, and microstructure of alkali-activated slag mixes representing concrete masonry blocks (CMBs). The carbonation curing process parameters varied, including initial curing duration, carbonation curing duration, and carbonation pressure. Research findings showed that a maximum CO₂ uptake of 12.8%, by binder mass, was attained upon exposing concrete to 4 h initial curing and 20 h carbonation curing at a pressure of 5 bars. The compressive strength and water absorption capacity improved with longer initial and carbonation curing durations and higher pressure. Upon subjecting to salt attack, the mass and strength of 28-day concrete samples increased, owing to the formation of Friedel’s salt and Halite. All mixes could be used as non-load-bearing CMB, with a 1-day strength greater than 4.1 MPa. Based on the global warming potential index, the carbon footprint of carbonation-cured, alkali-activated slag concrete masonry units was up to 46% lower than non-carbonation-cured counterparts. Research findings offer valuable information on the production of carbonation-cured, cement-free concrete masonry blocks to replenish natural resources, recycle industrial waste, and mitigate CO₂ emissions.