This paper focuses on the environmental leaching of antimony, a critical mineral, using deep eutectic solvents. Mining residues often contain embedded antimony, posing environmental risks. Deep eutectic solvents, known for being low in toxicity, cost-effective, and environmentally friendly, present a promising avenue for sustainable antimony extraction. The study focuses on optimizing the leaching process through experimental analysis by considering variables such as temperature, time, and percentage of solids. Different deep eutectic solvent (DES) compositions are being studied, including choline chloride with malonic acid, thiourea, and ethylene glycol in different molar ratios, to identify the most effective solvent system for antimony extraction. A sample, originally obtained from mining waste produced via the flotation of antimonite ore, was used to test these three types of DESs. By optimizing the leaching process by changing the ratio of solid and liquid components, as well as the amount of oxidizing agent up to 3 g, iodine, yields of up to 100% were achieved after leaching for 4 h at 100 °C. The aim of the study is to advance sustainable resource management by providing knowledge on an ecological and feasible method of extracting antimony from mine waste, leading to more conscious and efficient resource practices in the mining sector.

Geopolymers can improve environmental protection and are therefore considered a 21st-century material that requires special attention. The main objective of this study was to examine the utilization of fly ash deposited on a heap as a potential raw material for the geopolymerization process. In this work, flexural and compressive strengths, as well as water absorption of geopolymers, were evaluated based on alkaline activator properties. Na₂O content, SiO₂/Na₂O molar ratio and fly ash-to-water ratio were key observed factors. Mechanical strengths tests were conducted after 7, 28, 90, 180, and 360 days. The research findings showed that geopolymer cured at appropriate conditions and with a suitable alkaline activator can reach a compressive strength of more than 55 MPa. The presented study highlighted the possibility of the efficient use of fly ash to produce useful materials, i.e., geopolymers, which contribute to environmentally friendly solutions. This approach is fully in line with the principles of sustainable development.

This article will focus on the alkaline leaching of gold-bearing tetrahedrite concentrate in a solution containing sodium sulfide and sodium hydroxide. This selective leaching is followed by the leaching of heavy and waste metals into the solution, which may influence the physical properties and quality of the desired product, possibly causing environmental toxicity. At the same time, the amount of gold was observed during the leaching process to increase its content in the solid phase for the possibility of recovery and subsequent extraction of the precious metal. Sodium sulfide works very effectively on sulfide minerals which include tetrahedrite, and sodium hydroxide eliminates the hydrolysis of sulfur which slows leaching. The leaching kinetics were carried out with a duration of five hours, and based on volume sampling at certain time intervals from three samples, with the characteristic NaOH concentration, the leaching efficiency was observed from the results with atomic absorption spectrometry. The solid residue containing the tetrahedrite concentrate was analyzed through X-ray photoelectron analysis spectrometry, from which the % solids content was determined, and it is also known to deduce the leached amount of metals for each sample.