A straightforward method for the synthesis of CoFe _2.7 /CoFe ₂ O ₄ core/shell nanowires is described. The proposed method starts with a conventional pulsed electrodeposition procedure on alumina nanoporous template. The obtained CoFe _2.7 nanowires are released from the template and allowed to oxidize at room conditions over several weeks. The effects of partial oxidation on the structural and magnetic properties were studied by x-ray spectrometry, magnetometry, and scanning and transmission electron microscopy. The results indicate that the final nanowires are composed of 5 nm iron-cobalt alloy nanoparticles. Releasing the nanowires at room conditions promoted surface oxidation of the nanoparticles and created a CoFe ₂ O ₄ shell spinel-like structure. The shell avoids internal oxidation and promotes the formation of bi-magnetic soft/hard magnetic core/shell nanowires. The magnetic properties of both the initial single-phase CoFe _2.7 nanowires and the final core/shell nanowires, reveal that the changes in the properties from the array are due to the oxidation more than effects associated with released processes (disorder and agglomeration).

The influence of Nb doping was studied on ribbons of nominal composition Nd_yFe_86-x-yB₁₄Nb_x (y = 7, 8; x = 0, 2, 4). The alloys were prepared by melt-spinning and then annealed at 973 K for 20 minutes. The magnetic characterization revealed that niobium addition improves substantially the magnetic properties of the studied alloys. The structural characterization showed that, in most alloys, the magnetically hard phase Nd₂Fe₁₄B precipitated as the main phase. This was not the case for the ternaries (x = 0) and for the Nd₇Fe₇₇B₁₄Nb₂ alloys. Furthermore, the addition of Nb inhibited the precipitation of α-Fe, independently of the Nd content. From the complete set of samples studied in this work, we found that the sample with nominal composition Nd₈Fe₇₄B₁₄Nb₄ exhibited the highest coercive field H_C = 575 kA/m while Nd₇Fe₇₅B₁₄Nb₄ showed the highest maximum energy product, (BH)_max = 73 kJ/m³.