Flexible and binderless electrodes have become a promising candidate for the next generation of flexible power storage devices. However, developing high-performance electrode materials with high energy density and a long cycle life remains a serious challenge for sodium-ion batteries (SIBs). The main issue is the large volume change in electrode materials during the cycling processes, leading to rapid capacity decay for SIBs. In this study, flexible electrodes for a SnSb alloy–carbon nanofiber (SnSb@NC) membrane were successfully synthesized with the aid of hydrothermal, electrospinning and annealing processes. The as-prepared binderless SnSb@NC flexible anodes were investigated for the storage properties of SIBs at 500 °C, 600 °C and 700 °C (SnSb@NC-500, SnSb@NC-600 and SnSb@NC-700), respectively. And the flexible SnSb@NC-700 electrode displayed the preferable SIB performances, achieving 240 mAh/g after 100 cycles at 0.1 A g⁻¹. In degree-dependent I-V curve measurements, the SnSb@NC-700 membrane exhibited almost the same current at different bending degrees of 0°, 45°, 90°, 120° and 175°, indicating the outstanding mechanical properties of the flexible binderless electrodes.

WTe₂, a low-symmetry transition metal dichalcogenide, has broad prospects in functional device applications due to its excellent physical properties. When WTe₂ flake is integrated into practical device structures, its anisotropic thermal transport could be affected greatly by the substrate, which matters a lot to the energy efficiency and functional performance of the device. To investigate the effect of SiO₂/Si substrate, we carried out a comparative Raman thermometry study on a 50 nm-thick supported WTe₂ flake (with κ_zigzag = 62.17 W·m⁻¹·K⁻¹ and κ_armchair = 32.93 W·m⁻¹·K⁻¹), and a suspended WTe₂ flake of similar thickness (with κ_zigzag = 4.45 W·m⁻¹·K⁻¹, κ_armchair = 4.10 W·m⁻¹·K⁻¹). The results show that the thermal anisotropy ratio of supported WTe₂ flake (κ_zigzag/κ_armchair ≈ 1.89) is about 1.7 times that of suspended WTe₂ flake (κ_zigzag/κ_armchair ≈ 1.09). Based on the low symmetry nature of the WTe₂ structure, it is speculated that the factors contributing to thermal conductivity (mechanical properties and anisotropic low-frequency phonons) may have affected the thermal conductivity of WTe₂ flake in an uneven manner when supported on a substrate. Our findings could contribute to the 2D anisotropy physics and thermal transport study of functional devices based on WTe₂ and other low-symmetry materials, which helps solve the heat dissipation problem and optimize thermal/thermoelectric performance for practical electronic devices.