This research investigated the flexural behavior of high-strength steel (HSS)—concrete composite beams. The effect of concrete strength on the load-deflection behavior, flexural capacity, and ductility of HSS—concrete composite beams was investigated. Four full-scale HSS—concrete composite beam specimens were tested under static load. The test results demonstrate that the failure mode of HSS—concrete composite beams is flexural failure of the steel member and compression fracture of concrete at mid-span. The HSS—concrete composite beam exhibits good mechanical performance and deformation behavior. The ultimate bending strength and ductility of HSS—concrete composite beams were improved with the increased concrete strength. The theoretical results demonstrate that the simplified plastic method overestimates the ultimate bending strength of HSS—concrete composite beams. The main reason is that only a small part of the steel beam bottom shows plastic strengthening, which is not enough to make up for the strength loss caused by the steel near the neutral axis failure to yield and the relative interface slip. The nonlinear method based on material constitutive model could predict the load-bearing capacity accurately. After analyzing the ultimate bending capacity of 192 sample beams, the simplified plastic method was modified, and the theoretical method for ultimate bearing capacity of HSS—concrete composite beams was proposed.

Fiber reinforced polymer (FRP) has been proved to be effective to improve the structural strength and ductility for column structures. An experimental study was conducted to investigate the compressive performance of FRP confined glued-laminated timber (GLT) and cross-laminated timber (CLT) columns. A total of 60 column specimens of two dimensions in height using different FRP types, FRP thickness, and laminate types were tested under cyclic axial compression loads. This study focuses on the compressive capacity and ductility of the new FRP composited timber structure. For this purpose, a loading protocol was designed, including a force-dependent pre-load and an amplitude-increasing displacement-dependent cyclic compression load. The results showed that the ultimate compression load of specimens was considerably promoted by the FRP sheets. Wrapping FRP sheets led to an average improvement of 29% and 24% for the FRP confined CLT and GLT specimens, respectively, compared to the initial stiffness of unreinforced specimens. Using the FRP sheets, the energy dissipation capacity of CLT and GLT specimens was increased by 358% and 266%, respectively. In general, GLT specimens had a higher energy dissipation rate compared to the CLT specimens, while CLT specimens showed a better potential for sustained energy consumption if confined with sufficient FRP sheets.

In this research, experimental research and finite element modelling of glulam-concrete composite (GCC) beams were undertaken to study the flexural properties of composite beams containing timber board interlayers. The experimental results demonstrated that the failure mechanism of the GCC beam was the combination of bend and tensile failure of the glulam beam. The three-dimensional non linear finite element model was confirmed by comparing the load-deflection curve and load-interface slip curve with the experimental results. Parametric analyses were completed to explore the impacts of the glulam beam height, shear connector spacing, timber board interlayer thickness and concrete slab thickness on the flexural properties of composite beams. The numerical outcomes revealed that with an increase of glulam beam height, the bending bearing capacity and flexural stiffness of the composite beams were significantly improved. The timber boards were placed on top of the glulam members and used as the formwork for concrete slab casting. In addition, the flexural properties of composite beams were improved with the increase of the timber board thickness. With the elevation of the shear connector spacing, the ultimate bearing capacity and bending stiffness of composite beams were decreased. The bending bearing capacity and flexural rigidity of the GCC beams were ameliorated with the increase of concrete slab thickness.

Timber-concrete composite (TCC) beams are formed by integrating timber beams and concrete slabs into a cohesive structural unit using shear connectors. This integration capitalizes on the tensile strength of timber and the compressive strength of concrete, resulting in excellent load-bearing capacity, bending stiffness, vibration comfort, sound insulation, and fire resistance. The long-term behavior of TCC beams must be emphasized, considering the significant time-dependent behaviors of timber, concrete, and the connection system. This work analyzed the long-term mechanical behavior of TCC beams and systematically reviewed the current research on the long-term performance. The primary focus was on the experimental studies of the shear performance of the shear connectors and the mechanical performance of TCC beams under long-term loads. Furthermore, theoretical methods and numerical simulation analyses for evaluating the long-term performance of TCC beams were analyzed. Strengths and weaknesses of existing theoretical methods are identified, and further research and development in the calculation method of TCC beams under long-term loads is proposed.

Dowel connectors are extensively utilized to establish joint connections in timber constructions. This study investigated the embedment performance of glued laminated bamboo and timber composite joints through half-hole tests, focusing on the effects of dowel diameter, loading direction, contact condition, combination method, and moisture content. The experimental results indicated that the embedment strength of the specimens decreased progressively with an increase in dowel diameter. For wood–bamboo–wood (WBW) specimens, the embedment strength in the longitudinal to the grain was 18% higher than in the transverse direction. For bamboo–wood–bamboo (BWB), the embedment strength in the longitudinal to grain was 71% higher than in the transverse to grain. However, the compression direction to the grain had no observable impact on the embedment stiffness. The embedment capacity varied with different combination methods of bamboo and wood materials, and BWB specimens exhibited greater strength than WBW specimens. For WBW specimens, the embedment strength under smooth contact conditions was 61% higher than that under threaded contact conditions. Similarly, for BWB specimens, the embedment strength under smooth contact conditions was 73% higher than that under threaded contact conditions. After 3 days of water immersion, the embedment strength of glued laminated bamboo and timber composite specimens decreased to about 45% of the original strength. After 6 days of water immersion, the embedment strength of glued laminated bamboo and timber composite specimens fell to about 15% of the original strength. Based on the test results, this paper proposed calculation methods for predicting the embedment strength and stiffness of glued laminated bamboo and timber composite joints.