Mixed ionic-electronic conducting materials are not used as a single-layer electrolyte of solid oxide fuel cells (SOFCs) at relatively high operating temperatures of ~800 °C. This is because of a significant decrease in the open-circuit voltage (OCV) and, consequently, the SOFC power density. The paper presents a comparative analysis of the anode-supported SOFC properties obtained within the temperature range of 600 to 800 °C with yttria-stabilized zirconia (YSZ) electrolyte and gadolinium-doped ceria (GDC) electrolyte thin films. Electrolyte layers that are 3 µm thick are obtained by magnetron sputtering. It is shown that at 800 °C, the SOFC with the GDC electrolyte thin film provides an OCV over 0.9 V and power density of 2 W/cm². The latter is comparable to the power density of SOFCs with the YSZ electrolyte, which is a purely ionic conductor. The GDC electrolyte manifests the high performance, despite the SOFC power density loss induced by electronic conductivity of the former, which, in turn, is compensated by its other positive properties.

Samarium-doped ceria (SDC) is considered as an alternative electrolyte material for intermediate-temperature solid oxide fuel cells (IT-SOFCs) because its conductivity is higher than that of commonly used yttria-stabilized zirconia (YSZ). The paper compares the properties of anode-supported SOFCs with magnetron sputtered single-layer SDC and multilayer SDC/YSZ/SDC thin-film electrolyte, with the YSZ blocking layer 0.5, 1, and 1.5 μm thick. The thickness of the upper and lower SDC layers of the multilayer electrolyte are constant and amount to 3 and 1 μm, respectively. The thickness of single-layer SDC electrolyte is 5.5 μm. The SOFC performance is studied by measuring current–voltage characteristics and impedance spectra in the range of 500–800 °C. X-ray diffraction and scanning electron microscopy are used to investigate the structure of the deposited electrolyte and other fuel cell layers. SOFCs with the single-layer SDC electrolyte show the best performance at 650 °C. At this temperature, open circuit voltage and maximum power density are 0.8 V and 651 mW/cm², respectively. The formation of the SDC electrolyte with the YSZ blocking layer improves the open circuit voltage up to 1.1 V and increases the maximum power density at the temperatures over 600 °C. It is shown that the optimal thickness of the YSZ blocking layer is 1 µm. The fuel cell with the multilayer SDC/YSZ/SDC electrolyte, with the layer thicknesses of 3/1/1 µm, has the maximum power density of 2263 and 1132 mW/cm² at 800 and 650 °C, respectively.

Thin-film electrolyte made of 8-mol% yttria stabilized zirconia (8YSZ) for solid oxide fuel cells (SOFCs) was fabricated on anode substrates using reactive magnetron sputtering of Zr-Y targets in a mixture of Ar and O₂ gases. The deposition of 4–6 µm thin-film electrolyte was in the transition or oxide modes differing by the oxygen concentration in the sputtering atmosphere. The half-cell bending of the anode-supported SOFCs was measured to determine the residual stresses in the electrolyte films after the deposition and thermal annealing in air. The dependences were studied between the deposition modes, residual stresses in the films, and the SOFC performance. At 800 °C, the maximum power density of SOFCs ranged between 0.58 and 1.2 W/cm² depending on the electrolyte deposition mode. Scanning electron microscopy was carried out to investigate the surface morphology and structure of the YSZ electrolyte films after thermal annealing. Additionally, an X-ray diffraction analysis of the YSZ electrolyte films was conducted for the synchrotron radiation beam during thermal annealing at different temperatures up to 1300 °C. It was found that certain deposition modes provide the formation of the YSZ electrolyte films with acceptable residual stresses (<1 GPa) at room temperature, including films deposited on large area anodes (100 × 100 mm²).

Anode-supported solid oxide fuel cells with thin electrolytes show good electrochemical performance. In this work, 4-μm-thick YSZ electrolyte with 2-μm-thick GDC barrier layer is deposited onto the substrates by reactive magnetron sputtering. It is shown that high power density can be obtained for 5 × 5 cm² cells under planar stacks conditions with stainless steel current collectors. Electrochemical investigations are performed in the temperature range of 600-800°C. High power density of 0.29, 0.83, 1.4 W cm^-2 is achieved at a voltage 0.7 V and 600, 700, and 800°C, respectively.