This article describes GaN/AlN heterostructures for ultraviolet-C (UVC) emitters with multiple (up to 400 periods) two-dimensional (2D)-quantum disk/quantum well structures with the same GaN nominal thicknesses of 1.5 and 16 ML-thick AlN barrier layers, which were grown by plasma-assisted molecular-beam epitaxy in a wide range of gallium and activated nitrogen flux ratios (Ga/N₂*) on c-sapphire substrates. An increase in the Ga/N₂* ratio from 1.1 to 2.2 made it possible to change the 2D-topography of the structures due to a transition from the mixed spiral and 2D-nucleation growth to a purely spiral growth. As a result, the emission energy (wavelength) could be varied from 5.21 eV (238 nm) to 4.68 eV (265 nm) owing to the correspondingly increased carrier localization energy. Using electron-beam pumping with a maximum pulse current of 2 A at an electron energy of 12.5 keV, a maximum output optical power of 50 W was achieved for the 265 nm structure, while the structure emitting at 238 nm demonstrated a power of 10 W.

The decay kinetics of low-temperature exciton photoluminescence in a heterostructure with multiple GaN/AlN monolayer quantum wells, which is prepared by molecular beam epitaxy, is studied. Measured radiation decay curves are theoretically simulated within a three-level model. The relaxation of dipole-allowed “bright” excitons spatially confined in GaN monolayers is determined as exciton relaxation with a characteristic time of ~3 ps, which is accompanied by spin flip and by transformation to dipole-forbidden “dark” excitons whose levels lie by ~60 meV below in energy. It has been shown that exciton states at temperatures above 50 K are two-dimensional.

GaN/AlN heterostructures with thicknesses of one monolayer (ML) are currently considered to be the most promising material for creating UVC light-emitting devices. A unique functional property of these atomically thin quantum wells (QWs) is their ability to maintain stable excitons, resulting in a particularly high radiation yield at room temperature. However, the intrinsic properties of these excitons are substantially masked by the inhomogeneous broadening caused, in particular, by fluctuations in the QWs’ thicknesses. In this work, to reduce this effect, we fabricated cylindrical nanocolumns of 50 to 5000 nm in diameter using GaN/AlN single QW heterostructures grown via molecular beam epitaxy while using photolithography with a combination of wet and reactive ion etching. Photoluminescence measurements in an ultrasmall QW region enclosed in a nanocolumn revealed that narrow lines of individual excitons were localized on potential fluctuations attributed to 2-3-monolayer-high GaN clusters, which appear in QWs with an average thickness of 1 ML. The kinetics of luminescence with increasing temperature is determined via the change in the population of localized exciton states. At low temperatures, spin-forbidden dark excitons with lifetimes of ~40 ns predominate, while at temperatures elevated above 120 K, the overlying bright exciton states with much faster recombination dynamics determine the emission.