Zeolites in powder form have the potential to agglomerate, lowering access to active sites. Furthermore, a suspension of fine zeolite powder in liquid media is difficult to separate. Such drawbacks could be improved by dispersing zeolite crystals on support materials. This work demonstrates the dispersion of zeolite NaY crystals on bamboo wood by mixing the wood with zeolite gel before hydrothermal treatment. The syntheses were performed with acid-refluxed and non–refluxed wood. The phase of zeolites, particle distribution and morphology, zeolite content in the wood, and zeolite–wood interaction were investigated using X-ray diffraction, X-ray tomography, scanning electron microscopy, thermogravimetric analysis, nitrogen sorption analysis, and X-ray photoelectron spectroscopy. Higher zeolite content and better particle dispersion were obtained in the synthesis with the acid–refluxed wood. The composite of NaY on the acid-refluxed wood was demonstrated to be an effective adsorbent for Ni(II) ions in aqueous solutions, providing a higher adsorbed amount of Ni(II) per weight of NaY.

The reverse water–gas shift (RWGS) reaction is a promising route for converting CO₂ into CO, an important feedstock for synthetic fuels and chemicals. In this study, Zn–Co zeolitic imidazolate frameworks (ZIFs), including ZIF-8, ZIF-67, ZIF-67-8, and the core–shell structures ZIF-8@67 and ZIF-67@8, were synthesized as catalyst precursors and thermally activated prior to catalytic testing. Transmission electron microscopy and elemental mapping confirmed the formation of well-defined core–shell architectures, while synchrotron X-ray diffraction verified the characteristic sodalite-type framework. Thermogravimetric analysis revealed substantial framework decomposition during activation at 700 °C. In situ time-resolved X-ray absorption spectroscopy (TR-XAS) showed that Zn remained predominantly in the Zn²⁺ state throughout heating, whereas Co²⁺ underwent progressive reduction to metallic Co⁰ at temperatures approaching 600 °C. Ex situ X-ray absorption spectroscopy confirmed the presence of Zn²⁺ species and metallic cobalt after activation. Catalytic testing of the activated ZIF-derived materials showed that Co-containing catalysts exhibited significantly higher RWGS activity than Zn-only ZIF-8-derived catalyst. Among the investigated samples, ZIF-67@8_C-500 achieved the highest performance, producing 2.50 μmol CO (equivalent to 50 μmol g⁻¹ catalyst) at 600 °C with a H₂/CO₂ ratio of 2:1. The strong dependence of activity on ZIF-67 core loading indicates that metallic cobalt generated from the Co-rich core plays a dominant role in CO₂ conversion. Thermal activation transformed the highly porous ZIF precursors into metallic Co-containing carbonaceous catalysts. The resulting structural evolution, rather than retention of the original porous MOF framework, governed the catalytic performance in the RWGS reaction.