In the past decades, the durability of thermal barrier coatings (TBCs) has been extensively studied. The majority of researches emphasized the problem of oxidation, corrosion, and erosion induced by foreign object damage (FOD). TBCs with low thermal conductivity are usually coated on the hot-section components of the aircraft engine. The main composition of the TBCs is top-coat, which is usually regarded as a wear-resistant and heat-insulating layer, and it will significantly improve the working temperature of the hot-section components of the aircraft engine. The application of TBCs are serviced under a complex and rigid environment. The external parts of the TBCs are subjected to high-temperature and high-pressure loading, and the inner parts of the TBCs have a large thermal stress due to the different physical properties between the adjacent layers of the TBCs. To improve the heat efficiency of the hot-section components of aircraft engines, the working temperature of the TBCs should be improved further, which will result in the failure mechanism becoming more and more complicated for TBCs; thus, the current study is focusing on reviewing the failure mechanism of the TBCs when they are serviced under the actual high temperature conditions. Finite element simulation is an important method to study the failure mechanism of the TBCs, especially under some extremely rigid environments, which the experimental method cannot realize. In this paper, the research progress of the failure mechanism of TBCs at high temperature via finite element modeling is systematically reviewed.

This study focused on the numerical simulation of the distribution of residual stress in yttria-stabilized zirconia (YSZ) coatings prepared with atmospheric plasma spraying (APS). We particularly investigated the stress distribution around the interface between the top coat and bond coat. During thermal spray deposition, droplets and particles deposit on the substrate in a complex manner, causing interface waviness and non-uniform stress distribution. Therefore, residual stress is an important consideration when preparing thermal barrier coatings (TBCs). Residual stresses directly affect the performance of bond coats (BCs) and ceramic top coats (TCs). To accurately evaluate residual stress, we considered interface waviness and the thickness of the ceramic top coat and conducted a detailed analysis of stress distribution. The results show that compressive stress exists at the TC/BC interface, which may be caused by the mismatch in the thermal expansion coefficient between the YSZ top coat and the substrate, potentially leading to coating delamination. Moreover, the residual stress at the TC/BC interface significantly increases with an increasing YSZ thickness. When the top-coat thickness exceeds 300 μm, stress concentration and failure of the coating are likely to occur. Meanwhile, the optimized thermal spray experiment results confirm that the residual stress at the BC/YSZ interface of the thermal barrier coating is tensile stress, with a maximum value of 155 MPa, which is consistent with the finite element calculation results. Furthermore, the failure modes of TBCs with rough interface conditions are discussed in detail. Our research provides important guidance for TBC design and optimizing their performance.