In this overview, we summarize the results published to date concerning the small-scale mechanical testing of WC–Co cemented carbides and similar hardmetals, describing the clear trend in the research towards ever-smaller scales (currently at the nano-level). The load-size effect during micro/nanohardness testing of hardmetals and their constituents and the influence of the WC grain orientation on their deformation, hardness, indentation modulus, fracture toughness, and fatigue characteristics are discussed. The effect of the WC grain size/orientation, cobalt content, and testing environment on damage accumulation, wear mechanisms, and wear parameters are summarized. The deformation and fracture characteristics and mechanical properties, such as the yield and compression strength, of WC–Co composites and their individual WC grains at different orientations during micropillar compression tests are described. The mechanical and fracture properties of micro-cantilevers milled from WC–Co hardmetals, single WC grains, and cantilevers containing WC/WC boundaries with differently-oriented WC grains are discussed. The physical background of the deformation and damage mechanisms in cemented carbides at the micro/nano-levels is descri and potential directions for future research in this field are outlined.

In this overview, the results published to date concerning the development, processing, microstructure characteristics, and properties of silicon nitride/carbon nanotube (Si₃N₄ + CNTs) composites are summarized. The influence of the different processing routes on the microstructure development of the Si₃N₄ + CNTs is discussed. The effects of the CNTs addition on the mechanical properties—hardness, bending strength and fracture toughness—and tribological characteristics—wear rate and coefficient of friction—are summarized. The characteristic defects, fracture origins, toughening and damage mechanisms occurring during the testing are described. The influence of the CNTs’ addition on the thermal and functional properties of the composites is discussed as well. New trends in the development of these composites with significant potential for future applications are outlined.

Al₂O₃ + 30 vol% ZrO₂ matrix composites with 20 and 30 vol% cBN have been prepared with the optimized processing route, using spark plasma sintering (SPS) at temperatures of 1400 °C and 1250 °C. The influence of cBN addition on the microstructure characteristics, micro/nanohardness, elastic modulus, and crack-extension resistance of the composites and their constitutions have been investigated using scanning electron microscopy (SEM), statistical analyses of the individual grain size and micro/nanoindentation methods. The matrix consists of alumina and zirconia grains with grain sizes/diameter of approximately 220 and 160 nm with approximately 1.9 μm cBN grains in the Al₂O₃ + ZrO₂ + cBN composites. The microhardness is slightly increasing with cBN addition from 16.2 to 17.1 GPa and the crack-extension resistance from 3.72 to 4.29 MPa.m^1/2. The toughening mechanisms are in the form of crack deflection, crack branching, and crack bridging. The nanohardness and indentation modulus of the matrix are approximately 30 and 420 GPa, and the cBN grains 70 and 777 GPa, respectively.