Flammability testing of undergarments is a topic that is often overlooked and rarely on the list of textiles to be tested for fire safety. However, it is particularly important for professionals exposed to fire risk to investigate the flammability of underwear as its direct contact with the skin can be critical to the extent and degree of skin burns. This research focuses on the suitability of affordable blends of 55 wt.% modacrylic, 15 wt.% polyacrylate, and 30 wt.% lyocell fibres that have the potential to be used for flame-resistant underwear. The influence of modacrylic fibre linear density (standard and microfibres), ring spinning processes (conventional, Sirospun, and compact), and knitted structure (plain, 2:1 rib, 2:1 tuck rib, single pique, and triple tuck) on their properties required for thermal comfort in high-temperature environments was investigated. Scanning electron and optical microscopy, FT-IR spectroscopy, mechanical testing, moisture regain, water sorption, wettability, absorption, DSC, TGA, and flammability were tested to assess the desired suitability. The wetting time (5–14.6 s) and water absorption time (4.6–21.4 s) of the knitted fabrics have shown excellent ability to transport and absorb water compared to the knitted fabrics created from a conventional blend of 65% modacrylic and 35% cotton fibres. The afterflame and afterglow times of less than 2 s met the criteria for non-flammability of the knitted fabrics according to the limited flame spread test method. The results show that the investigated blends have the potential to be used for affordable flame-retardant and thermally comfortable knitted fabrics for underwear.

The aim of this research was to determine the optimum twist equation for ring-spun yarns. The yarn twist can be calculated by different equations. With the research, we tried to find the appropriate equation to determine the yarn twist, which is determined by the values of yarn strength and hairiness. In the research, yarns from long staple combed cotton rovings and of different fineness (10 tex, 11.8 tex, 20 tex and 29.4 tex) were analyzed. The yarn twist was calculated using the equations of Koechlin and Laetsch. The analyzed yarns were produced in the spinning mill on the laboratory ring spinning machine Spinntester. In the second part of the investigation, yarn strength and hairiness were analyzed as a function of yarn twist. The results showed that Laetsch’s equation is suitable for determining the twist for yarns with a fineness of 10 tex, 11.8 tex, 20 tex and 29.4 tex, since, in this case, the calculated number of yarn threads is higher and thus the strength and elongation at break are also higher. The yarn hairiness is higher in analyzed samples for yarns with the twist calculated according to the Koechlin’s equation.