Water splitting technology is an innovative strategy to face the dependency on fossil fuels and, at the same time, address environmental pollution issues. Electrocatalysts seem to be the better option to improve water separation efficiency and satisfy the commercial-scale demand for hydrogen. Therefore, the design and fabrication of heterostructures with a high affinity for achieving water splitting have been proposed. In this review, the application of several electrocatalysts for hydrogen and oxygen evolution reactions is presented and discussed in detail. A review of the recent advances in water separation using noble metals such as Pt-, Ir-, and Ru-based electrodes is presented, followed by a highlighting of the current trends in noble-metal-free electrocatalysts and novel preparation methods. Furthermore, it contemplates some results of a hybrid organic molecule–water electrolysis and photoelectrochemical water splitting. This review intends to give insight into the main trends in water splitting and the barriers that need to be overcome to further boost the efficiency of the main hydrogen and oxygen generation systems that ultimately result in large-scale applications. Finally, future challenges and perspectives are addressed, considering all the novelties and the proposed pathways for water splitting.

A SrTiO3 electroceramic with perovskite structure was produced by the calcination of a mixture of SrCO3 and TiO2 intensively grounded by high energy milling. For this purpose, raw materials were mixed in stoichiometric amounts in a planetary type mill; the obtained powder mixture was calcined for 2 h at temperatures between 800 and 1300°C. Samples resulting from the calcination were characterized by XRD, FTIR, SEM analysis and electrical measurements. From XRD, it was determined that the SrTiO3 formed presents the cubic structure of perovskite. The complete reaction for SrTiO3 compound formation occurs at 1200°C. Micrograph observations indicate the presence of a homogeneous microstructure with tiny grain size. The measured values of electrical resistivity were within the typical range of insulating materials.

Microwave range had been widely used for heating processes. In this work theoretical and experimental results on manufacturing of expandable polystyrene using specific frequencies of 2.45GHz are presented. Simulations of temperature distribution were performed using the software Comsol Multiphysics®. In order to increase the material absorption to microwaves, several solvents as ethanol, a mixture of ethanol/water and hydrogen peroxide were tested. Temperature distribution inside material was measured with an infrared laser sensor. Microwave heating allows Expanded Polystyrene Styrofoam (EPS) molding in 180seconds, reaching a considerable manufacturing time reduction compared with traditional processes where drying time may take up to one day