To contribute to solving global energy problems, a multifunctional CoFe₂O₄ spinel was synthesized and used as a catalyst for overall water splitting and as an electrode material for supercapacitors. The ultra-fast one-step electrodeposition of CoFe₂O₄ over conducting substrates provides an economic pathway to high-performance energy devices. Electrodeposited CoFe₂O₄ on Ni-foam showed a low overpotential of 270 mV and a Tafel slope of 31 mV/dec. The results indicated a higher conductivity for electrodeposited compared with dip-coated CoFe₂O₄ with enhanced device performance. Moreover, bending and chronoamperometry studies suggest excellent durability of the catalytic electrode for long-term use. The energy storage behavior of CoFe₂O₄ showed high specific capacitance of 768 F/g at a current density of 0.5 A/g and maintained about 80% retention after 10,000 cycles. These results demonstrate the competitiveness and multifunctional applicability of the CoFe₂O₄ spinel to be used for energy generation and storage devices.

The tackling of carbon deposition during the dry reforming of biogas (BDR) necessitates research of the surface of spent catalysts in an effort to obtain a better understanding of the effect that different carbon allotropes have on the deactivation mechanism and correlation of their formation with catalytic properties. The work presented herein provides a comparative assessment of catalytic stability in relation to carbon deposition and metal particle sintering on un-promoted Ni/Al₂O₃, Ni/ZrO₂ and Ni/SiO₂ catalysts for different reaction temperatures. The spent catalysts were examined using thermogravimetric analysis (TGA), Raman spectroscopy, high angle annular dark field scanning transmission electron microscopy (STEM-HAADF) and X-ray photoelectron spectroscopy (XPS). The results show that the formation and nature of carbonaceous deposits on catalytic surfaces (and thus catalytic stability) depend on the interplay of a number of crucial parameters such as metal support interaction, acidity/basicity characteristics, O^2– lability and active phase particle size. When a catalytic system possesses only some of these beneficial characteristics, then competition with adverse effects may overshadow any potential benefits.