The optimization of a broach surface is of great significance to improve the cutting performance of the tool. However, the traditional optimization method (surface texture, coating, etc.) destroys the stress distribution of the tool and reduces the service life of the tool. To avoid these problems, four kinds of flocking surfaces (FB1, FB2, FB3, and FB4), imitating the biological structure of Daphniphyllum calycinum Benth (DCB), were fabricated on the rake face of the broach by electrostatic flocking. The broaching experiment, wettability, and spreading experiment were then conducted. Moreover, the mathematical model of the friction coefficient of the bionic broach was built. The effect of broaches with different flocking surfaces on the broaching force, chip morphology, and surface quality of workpieces was studied. The results indicate that the flocked broaches (FB) with good lubricity and capacity of microchips removal (CMR) present a smaller cutting force (F_c) and positive pressure (F_t) compared to the unflocked broach (NB), and reduce the friction coefficient (COF). The chip curl was decreased, and the shear angle was increased by FB, which were attributed to the function of absorbing lubricant, storing, and sweeping microchips. Its vibration suppression effect enhanced the stability in the broaching process and improved the surface quality of the workpiece. More importantly, the FB2 with the most reasonable fluff area and spacing exhibited the best cutting performance. The experimental conclusions and methods of this paper can provide a new research idea for functional structure tools.

YG8 is a common cemented carbide material with excellent mechanical properties and mechanical properties, so it is widely used in the actual industry. However, due to the active chemical properties and strong affinity of tungsten alloy steel, it is easy to produce bonding and peeling in application, resulting in an unstable process and short service life. In order to control and reduce the surface wear of YG8 cemented carbide, groove-textured surface (GS) and flocking surface (FS) were prepared on smooth surface (SS). The friction characteristics of the samples were studied under different applied load conditions. The results show that the average friction coefficient of SS, GS and FS is inversely proportional to the load in dry/oil environment. Compared with SS, FS exhibits the lowest friction coefficient, which is reduced by 30.78% (dry friction) and 13.13% (oil lubrication). FS effectively improves the tooth jump phenomenon of the sample and the amplitude of the friction coefficient, friction force and load, and has the best anti-friction characteristics. At the same time, the FS with the fastest contact angle drop at any time also showed excellent wetting ability, and the wear rate decreased by an order of magnitude. The implantation of fibers in the groove inhibits the spalling and furrow of wear track, which is attributed to the effect of fibers on damage repair. In the friction process, FS increases the content of the O element and induces the formation of oxides. The friction mechanism is mainly chemical wear. The excellent tribological properties of FS have a good guiding significance and theoretical support for improving the tribological properties of high hardness material surfaces.

This paper presents a breakthrough in activating the skin effect at conventional broaching speeds (1–8 m/min) by using laser defocus gradient modification to induce surface embrittlement in martensitic stainless steel Z10C13. Through controlled defocusing, a 50 μm gradient remelting layer was created, which features ultrafine grains (0.8 μm) and a high-density geometrically necessary dislocation (GND) zone (ρGND = 2.27 μm⁻³). The quasi-cleavage fracture was triggered via dislocation pinning by non-oriented low-angle grain boundaries (28.4% LAGBs). Multiscale characterization confirms that this microstructural transformation enhances surface hardness by 12.95% (reaching 31.4 HRC), reduces cutting force by 34.07%, and improves surface roughness by 63.74% (Sz = 28.80 μm). Simultaneously, a parallel crack-deflection mechanism restricts subsurface damage propagation, resulting in a crack-free subsurface zone. These results demonstrate the effectiveness of the embrittlement–toughening dichotomy for precision machining of difficult-to-cut materials under low-speed constraints.

Considering that the ferritic stainless steel Z10C13 support plate material in nuclear power equipment tends to undergo fretting wear during service, this paper systematically investigates the effect of varying normal loads (10–50 N) and displacement amplitudes (15–75 μm) on its fretting response and wear mechanisms. Through ball-on-flat fretting wear experiments, together with macro- and micro-scale observations of wear scars, it is revealed that normal load primarily controls the contact intensity and the extent of adhesion, whereas displacement amplitude mainly affects the slip amplitude and features of fatigue damage. The results show that the fretting system’s dissipated energy increases nonlinearly with both load and amplitude, and their coupled effect significantly exacerbates interfacial damage. The wear scar morphology evolves from a shallow bowl shape to a structure characterized by multiple spalling pits and propagating fatigue cracks. An equivalent hardness-corrected Archard model is proposed based on the experimental data. The model captures the nonlinear dependence of equivalent material hardness on both load and amplitude. As a result, it accurately predicts wear volume ($R^2=0.9838$), demonstrating its physical consistency and modeling reliability. Overall, this study elucidates the multi-scale damage evolution mechanism of Z10C13 under fretting conditions and provides a theoretical foundation and methodological support for wear-resistant design, life prediction, and safety evaluation of nuclear power support structures.