We developed an implant combined with both antitumor and bone regeneration functions.

Endowing implant surfaces with combined antibacterial and osteogenic properties by drug-loaded coatings has made great strides, but how to achieve the combined excellence of infection-triggered bactericidal and in vivo-proven osteogenic activities without causing bacterial resistance still remains a formidable challenge. Herein, antimicrobial peptides (AMPs) with osteogenic fragments were designed and complexed on the surface of silver nanoparticle (AgNP) through hydrogen bonding, and the collagen structure-bionic silk fibroin (SF) was applied to carry AgNPs@ AMPs to achieve infection-triggered antibacterial and osteointegration. As verified by TEM, AMPs contributed to the dispersion and size-regulation of AgNPs, with a particle size of about 20 nm, and a clear protein corona structure was observed on the particle surface. The release curve of silver ion displayed that the SF-based coating owned sensitive pH-responsive properties. In the antibacterial test against S.aureus for up to 21 days, the antibacterial rate had always remained above 99%. Meanwhile, the underlying mechanism was revealed, originating from the destruction of the bacterial cell membranes and ROS generation. The SF-based coating was conducive to the adhesion, diffusion, and proliferation of bone marrow stem cells (BMSCs) on the surface, and promoted the expression of osteogenic genes and collagen secretion. The in vivo implantation results showed that compared with the untreated Ti implants, SF-based coating enhanced osseointegration at week 4 and 8. Overall, the AgNPs@AMPs-loaded SF-based coating presented the ability to synergistically inhibit bacteria and promote osseointegration, possessing tremendous potential application prospects in bone defects and related-infection treatments.

Tantalum (Ta) metal is receiving increasing interest as biomaterial for load-bearing orthopedic applications and the synthetic properties of Ta can be tailored by altering its grain structures. This study evaluates the capability of sliding friction treatment (SFT) technique to modulate the comprehensive performances of pure Ta. Specifically, novel nanocrystalline (NC) surface with extremely small grains (average grain size of ≤20 nm) was fabricated on conventional coarse-grained (CG) Ta by SFT. It shows that NC surface possessed higher surface hydrophilicity and enhanced corrosion resistance than CG surface. Additionally, the NC surface adsorbed a notably higher percentage of protein as compared to CG surface. The in vitro results indicated that in the initial culture stages (up to 24 h), the NC surface exhibited considerably enhanced osteoblast adherence and spreading, consistent with demonstrated superior hydrophilicity on NC surface. Furthermore, within the 14 days culture period, NC Ta surface exhibited a remarkable enhancement in osteoblast cell proliferation, maturation and mineralization as compared to CG surface. Ultimately, the improved osteoblast functions together with the good mechanical and anti-corrosion properties render the SFT-processed Ta a promising alternative for the load-bearing bone implant applications.