This work reports the influence of a reduced graphene oxide (rGO) support on the catalytic performance of Cu@PtRu/rGO electrocatalysts toward methanol oxidation in an acidic medium. These electrocatalysts are synthesized via a two-step reduction method; the first step utilizes ethylene glycol for the reduction of Cu²⁺ ions, forming Cu/rGO. In the second step, spontaneous redox reactions take place, in a process known as galvanic displacement, where the Pt²⁺ and Ru³⁺ species are reduced to form PtRu layers, and the copper is partially oxidized to the solution. Then, the Cu@PtRu/rGO core–shell is produced, comprising Cu in the inner structure (core) and PtRu on the outer part (shell). To compare the catalytic performance of the prepared nanocatalysts (NCs), Pt/C, PtRu/C, and Cu@PtRu/C are also synthesized on Vulcan XC-72R carbon. All catalysts are characterized via X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). Cyclic voltammetry (CV) and chronoamperometry (CA) are employed to measure the electrochemical performance. The core–shell/rGO combination is superior in catalytic activity to the traditional Pt/C, PtRu/C, and Cu@PtRu/C catalysts for the methanol oxidation reaction. These results suggest that Cu@PtRu/rGO exhibits a high bulk activity for methanol electrooxidation, a high stability, and a high tolerance to CO poisoning, meaning it is possible to reduce the platinum loading in proton-exchange membrane fuel cells (PEMFCs).

This work reports the influence of reduced graphene oxide (rGO) support on the catalytic performance of Cu@PtRu/rGO catalysts towards methanol oxidation in acidic medium. These core-shell catalysts are synthesized by the reduction method in two steps being the first using ethylene glycol to obtain Cu/rGO and the second, the reduction of copper atoms synthesized in the previous step to produce Cu@PtRu/rGO. In order to compare the catalytic performance of the prepared catalysts, Pt/C, PtRu/C, Cu@PtRu/C catalysts are also synthesized on Vulcan XC-72R carbon. The theoretical loading of Pt used in the Vulcan XC-72R carbon supported catalysts is equal to that utilized in Cu@PtRu/rGO, and higher in the other prepared catalysts. The surface composition of the nanoparticles, as well as their sizes, particle size distribution and morphology of the catalyst particles are characterized by X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). Cyclic voltammetry (CV) and chronoamperometry (CA) are employed to measure the electrochemical performance of the prepared catalysts. The anodic scans show that for the region of technological interest (0.1 to 0.4 V), the Cu@PtRu/rGO-16 electrocatalyst exhibits higher current density value than the others as a result of its lower starting oxidation potential (0.250V against 0.437V for Pt/C) and its higher ratio between forward (iF) and reverse (iR) current densities (iF/iR 1.45 against 0.93 for Pt/C). Chronoamperometric tests depict that the current density value of Cu@PtRu/rGO-16 catalyst is about 4 times higher than that of Cu@PtRu/C-16 and Cu@PtRu/C-18 catalysts, ca. 4.8 times higher than that of PtRu/C-30 catalyst and around 6 times higher than that of Pt/C-30. These results suggest that Cu@PtRu/rGO-16 exhibits high bulk activity for the electrooxidation of methanol, high stability and high tolerance to CO poisoning, making it possible to reduce the platinum loading in proton exchange membrane fuel cells (PEMFCs).