The plasma-enhanced chemical vapor (PECVD) co-deposition of pyridine and 1,2 dicarbadodecaborane, 1,2-B ₁₀ C ₂ H ₁₂ (orthocarborane) results in semiconducting boron carbide composite films with a significantly better charge extraction than plasma-enhanced chemical vapor deposited semiconducting boron carbide synthesized from orthocarborane alone. The PECVD pyridine/orthocarborane based semiconducting boron carbide composites, with pyridine/orthocarborane ratios ~3:1 or 9:1 exhibit indirect band gaps of 1.8 eV or 1.6 eV, respectively. These energies are less than the corresponding exciton energies of 2.0 eV–2.1 eV. The capacitance/voltage and current/voltage measurements indicate the hole carrier lifetimes for PECVD pyridine/orthocarborane based semiconducting boron carbide composites (3:1) films of ~350 µ s compared to values of ⩽35 µ s for the PECVD semiconducting boron carbide films fabricated without pyridine. The hole carrier lifetime values are significantly longer than the initial exciton decay times in the region of ~0.05 ns and 0.27 ns for PECVD semiconducting boron carbide films with and without pyridine, respectively, as suggested by the time-resolved photoluminescence. These data indicate enhanced electron–hole separation and charge carrier lifetimes in PECVD pyridine/orthocarborane based semiconducting boron carbide and are consistent with the results of zero bias neutron voltaic measurements indicating significantly enhanced charge collection efficiency.

Plasma-enhanced chemical vapor (PECVD) codeposition of benzene and 1,2-dicarbadodecaborane, 1,2-B10C2H12 (orthocarborane) and benzene, 1,7 dicarbadodecaborane, and 1,7-B10C2H12 (metacarborane) results in semiconducting boron carbide composite films with significantly longer drift carrier lifetimes than plasma-enhanced chemical vapor deposited semiconducting boron carbide synthesized from orthocarborane or metacarborane alone. Capacitance versus voltage C(V) and current versus voltage I(V) measurements indicate the hole carrier lifetimes for PECVD benzene/orthocarborane based semiconducting boron carbide composites increase to 2.5 ms from values of ≤35 μs for the PECVD semiconducting boron carbide films fabricated without benzene. For PECVD benzene/metacarborane based semiconducting boron carbide composites, there is an increase in the hole carrier lifetime to roughly 300 ns from values of 50 ns for those films fabricated without benzene.