In this study, the use of cotton fiber (CF) as a filler in poly(butylene succinate) (PBS) and the effect of silane treatment on the mechanical properties, thermal stability, and biodegradability of PBS/CF composites are investigated. The results showed that the tensile strength of PBS was improved (15%–78%) with the incorporation of CF (10–40 wt%) and was further increased (25%–118%) when CF was treated with a silane coupling agent. Scanning electron microscopy (SEM) observation of the fracture surfaces of PBS/CF composites showed that there was slight improvement in fiber-matrix compatibility. Thermogravimetric (TG) analysis showed that the thermal stability of the composites was lower than that of neat PBS and decreased with increasing filler loading. The biobased carbon content of the composites increased with increasing CF content. The incorporation of CF (with and without silane treatment) in PBS significantly increased the biodegradation rate of the composites.

Biodegradabilities of polymers and their composites in a controlled compost were described. Polycaprolactone (PCL) and poly(lactic acid) (PLA) were employed as biodegradable polymers. Biodegradabilities of PCL and PLA samples in a controlled compost were measured using a Microbial Oxidative Degradation Analyzer (MODA) according to ISO 14855-2. Sample preparation method for biodegradation test according to ISO/DIS 10210 was also described. Effects of sizes and shapes of samples on biodegradability were studied. Reproducibility of biodegradation test of ISO 14855-2 by MODA was confirmed. Validity of sample preparation method for polymer pellets, polymer film, and polymer products of ISO/DIS 10210 for ISO 14855-2 was confirmed.

Anaerobic biodegradation tests of poly(lactic acid) (PLA) powder were done at the thermophilic (55 °C) and mesophilic temperature (35 °C) under aquatic conditions [total solid concentrations of the used sludge were 2.07% (at 55 °C) and 2.24% (at 35 °C)] using a newly developed evaluation system. With this system, the evolved biogas is collected in a gas sampling bag at atmospheric pressure. This method is more convenient than using a pressure transducer or inverted graduated cylinder submerged in water. PLA was degraded about 60% in 30 days, about 80% in 40 days and about 90% in 60 days at 55 °C. On the other hand, the PLA degradation started in 55 days at 35 °C and degradation rate was much slower than at 55 °C.

The biodegradabilities of poly(butylene succinate) (PBS) powders in a controlled compost at 58 °C have been studied using a Microbial Oxidative Degradation Analyzer (MODA) based on the ISO 14855-2 method, entitled “Determination of the ultimate aerobic biodegradability of plastic materials under controlled composting conditions—Method by analysis of evolved carbon dioxide—Part 2: Gravimetric measurement of carbon dioxide evolved in a laboratory-scale test”. The evolved CO₂ was trapped by an additional aqueous Ba(OH)₂ solution. The trapped BaCO₃ was transformed into graphite via a serial vaporization and reduction reaction using a gas-tight tube and vacuum manifold system. This graphite was analyzed by accelerated mass spectrometry (AMS) to determine the percent modern carbon [pMC (sample)] based on the ¹⁴C radiocarbon concentration. By using the theory that pMC (sample) was the sum of the pMC (compost) (109.87%) and pMC (PBS) (0%) as the respective ratio in the determined period, the CO₂ (respiration) was calculated from only one reaction vessel. It was found that the biodegradabilities determined by the CO₂ amount from PBS in the sample vessel were about 30% lower than those based on the ISO method. These differences between the ISO and AMS methods are caused by the fact that part of the carbons from PBS are changed into metabolites by the microorganisms in the compost, and not changed into CO₂.