The manuscript demonstrates the structure and the mechanical behavior of a material manufactured by multilayer arc deposition. Three-dimensional printing was performed using OK Autrod 13.14 wire on a substrate of heat-resistant 12Cr1MoV steel in the standard gas metal arc welding (GMAW) mode and in the coldArc mode with reduced heat input. The printed materials have 40–45% higher strength and 50–70% lower ductility compared to the substrate. The microhardness of the printed materials is higher than the substrate, but it is reduced at the transition regions between the deposited layers. These regions have been studied using optical microscopy and digital image correlation. Such layer boundaries are an additional factor in reducing the plasticity of the material. The increase in strength and decrease in ductility for printed materials compared to the ferrite–pearlitic substrate is associated with a high cooling rate and the formation of a mixture of acicular and allotriomorphic ferrite, which have higher hardness. The structure of the obtained layers along the height is non-uniform and undergoes changes during the deposition of new layers. The main difference between the 3D printing modes is the reduced heat input in the coldArc mode, which results in less heat accumulation and faster cooling of the wall. Thus, a more dispersed and solid structure was formed compared with GMAW. It was concluded that the cooling rate and the level of heat input are the main factors affecting the structure formation (martensitic, bainitic, or ferritic), the height and quality of the surface, and the mechanical properties of the printed wall.

Влияние режимов поперечно-винтовой прокатки на механические свойства и вязкость разрушения трубной стали