This study investigated the relationship between the structure and mechanical properties of polycaprolactone (PCL) nanocomposites reinforced with baghdadite, a newly introduced bioactive agent. The baghdadite nanoparticles were synthesised using the sol–gel method and incorporated into PCL films using the solvent casting technique. The results showed that adding baghdadite to PCL improved the nanocomposites’ tensile strength and elastic modulus, consistent with the results obtained from the prediction models of mechanical properties. The tensile strength increased from 16 to 21 MPa, and the elastic modulus enhanced from 149 to 194 MPa with fillers compared to test specimens without fillers. The thermal properties of the nanocomposites were also improved, with the degradation temperature increasing from 388 °C to 402 °C when 10% baghdadite was added to PCL. Furthermore, it was found that the nanocomposites containing baghdadite showed an apatite-like layer on their surfaces when exposed to simulated body solution (SBF) for 28 days, especially in the film containing 20% nanoparticles (PB20), which exhibited higher apatite density. The addition of baghdadite nanoparticles into pure PCL also improved the viability of MG63 cells, increasing the viability percentage on day five from 103 in PCL to 136 in PB20. Additionally, PB20 showed a favourable degradation rate in PBS solution, increasing mass loss from 2.63 to 4.08 per cent over four weeks. Overall, this study provides valuable insights into the structure–property relationships of biodegradable-bioactive nanocomposites, particularly those reinforced with new bioactive agents.

There is an essential clinical need to develop rapid process scaffolds to repair bone defects. The current research presented the development of calcium zirconium silicate/polycaprolactone for bone tissue engineering utilising melt extrusion-based 3D printing. Calcium zirconium silicate (CZS) nanoparticles were added to polycaprolactone (PCL) porous scaffolds to enhance their biological and mechanical properties, while the resulting properties were studied extensively. No significant difference was found in the melting point of the samples, while the crystallisation temperature points of the samples containing bioceramic increased from 36.1 to 40.2 °C. Thermal degradation commenced around 350 °C for all materials. According to our results, increasing the CZS content from 0 to 40 wt.% (PC40) in porous scaffolds (porosity about 55–62%) improved the compressive strength from 2.8 to 10.9 MPa. Furthermore, apatite formation ability in SBF solution increased significantly by enhancing the CZS percentage. According to MTT test results, the viability of MG63 cells improved remarkably (~29%) in PC40 compared to pure PCL. These findings suggest that a 3D-printed PCL/CZS composite scaffold can be fabricated successfully and shows great potential as an implantable material for bone tissue engineering applications.

This study investigated the impact of temperature, time, and homogenisation on the transient liquid phase bonding of Inconel 617 to stainless steel 310, employing AWS BNI2 foil as an interlayer. Nine test series were conducted at temperatures of 1050 °C and 1100 °C, with bonding durations ranging from 10 to 60 min. The homogenisation process was carried out on specimens that underwent full isothermal solidification at a temperature of 1170 °C for 180 min. The microscopic analysis indicated that extending the time and raising the bonding temperature resulted in the extension of the isothermal solidified zone, accompanied by a reduction in the quantity of eutectic phases. Complete isothermal solidification was seen exclusively in samples bonded at temperatures of 1050 °C for 60 min and 1100 °C for a duration of 50 min. The size of the diffusion-affected zone expanded as the bonding temperature and duration rose, but the presence of brittle intermetallic phases diminished. The microstructure of the homogenised sample indicated that the diffusion-affected zone had been almost completely eliminated. Hardness variations indicated heightened hardness in the diffusion-affected zone (DAZ) and athermal solidified zone (ASZ). Shear strength is maximised in homogenised specimens with minimised ASZ.