This paper investigates the effect of decorating graphene with zinc oxide (ZnO) nanoparticles (NPs) for the detection of NO₂. In this regard, two graphene sensors with different ZnO loadings of 5 wt.% and 20 wt.% were prepared, and their responses towards NO₂ at room temperature and different conditions were compared. The experimental results demonstrate that the graphene loaded with 5 wt.% ZnO NPs (G95/5) shows better performance at detecting low concentrations of the target gas than the one loaded with 20 wt.% ZnO NPs (G80/20). Moreover, measurements under dry and humid conditions of the G95/5 sensor revealed that the material is very sensitive to ambient moisture, showing an almost eight-fold increase in NO₂ sensitivity when the background changes from dry to 70% relative humidity. Regarding sensor selectivity, it presents a significant selectivity towards NO₂ compared to other gas compounds.

Nanosized manganese dioxide (MnO₂) material has been successfully incorporated into a graphene oxide (GO) sensitive layer. Since this type of heterojunction has never been reported in the literature related to gas sensing, these sensors were prepared, tested, and reported. The morphological properties and composition of the MnO₂@GO material have been thoroughly studied via FESEM, XRD, Raman spectroscopy, HR-TEM, and ATR-IR. Gas sensitivity and selectivity towards mainly NO₂ and other gases (NH₃, CO, ethanol, benzene, and H₂) have also been studied. The obtained sensors were exposed to different concentrations of NO₂ ranging from 200 ppb to 1000 ppb at 150 °C and under close to real conditions (25% relative humidity and 70% relative humidity). The MnO₂@GO sensors have shown a high response of 16.3% towards 1 ppm of NO₂ under dry conditions and a higher response of 44% at 70% RH towards the same concentration. Finally, it has also shown a strong sensitivity for NO₂.

Manganese dioxide (MnO₂) has drawn attention as a sensitiser to be incorporated in graphene-based chemoresistive sensors thanks to its promising properties. In this regard, a rGO@MnO₂ sensing material was prepared and deposited on two different substrates (silicon and Kapton). The effect of the substrate nature on the morphology and sensing behaviour of the rGO@MnO₂ material was thoroughly analysed and reported. These sensors were exposed to different dilutions of NO₂ ranging from 200 ppb to 1000 ppb under dry and humid conditions (25% RH and 70% RH) at room temperature. rGO@MnO₂ deposited on Kapton showed the highest response of 6.6% towards 1 ppm of NO₂ under dry conditions at RT. Other gases or vapours such as NH₃, CO, ethanol, H₂ and benzene were also tested. FESEM, HRTEM, Raman, XRD and ATR-IR were used to characterise the prepared sensors. The experimental results showed that the incorporation of nanosized MnO₂ in the rGO material enhanced its response towards NO₂. Moreover, this material also showed very good responses toward NH₃ both under dry and humid conditions, with the rGO@MnO₂ sensor on silicon showing the highest response of 18.5% towards 50 ppm of NH₃ under 50% RH at RT. Finally, the synthetised layers showed no cross-responsiveness towards other toxic gases.

Increasing the energy density and power of supercapacitors through hybrids of carbonaceous materials and metal oxides continues to be the subject of numerous research works. The correlation between specific capacitance and the properties of materials used as electrodes attracts great interest. In the present study, we investigated composites (GO/Mn₃O₄) prepared by the hydrothermal method with a variable ratio of GO/Mn₃O₄ and tested them as supercapacitor electrode materials in three- and two-electrode cells. The chemical characterization carried out by X-ray photoelectron spectroscopy and the adsorption techniques used allowed the determination of the surface carbon and oxygen content, as well as its textural properties. In this work, we analyzed the contribution of the double layer and the Faradaic reactions to the value of the final capacitance of the synthesized materials. Beyond empirically obtaining the electrochemical properties, these have been related to the physicochemical characteristics of the hybrids to help design materials with the best performance for supercapacitor electrodes.

Manganese dioxide (MnO2) has drawn attention as a sensitizer to be incorporated in graphene-based chemoresistive sensors thanks to its promising properties. In this regard, a rGO@MnO2 sensing material was prepared and deposited on two different substrates (Silicon and Kapton). These sensors were exposed to different dilutions of NO2 under dry and humid conditions at room temperature. Other gases or vapours such as NH3, CO, ethanol and H2 were also tested. FESEM, HRTEM, RAMAN and XRD were used to characterize the prepared sensors. The experimental results showed that the incorporation of MnO2 in the rGO material enhanced its response towards NO2. Moreover, this material showed also very good responses toward NH3 both under dry and humid conditions and showed no cross-responsiveness towards other toxic gases.