A hybrid alginate hydrogel–chitosan nanoparticle system suitable for biomedical applications was prepared. Chitosan (CS) was used as a matrix for the encapsulation of lavender (Lavandula angustifolia) essential oil (LEO) and Mentha (Mentha arvensis) essential oil (MEO). An aqueous solution of an acidic Natural Deep Eutectic Solvent (NADES), namely choline chloride/ascorbic acid in a 2:1 molar ratio, was used to achieve the acidic environment for the dissolution of chitosan and also played the role of the ionic gelator for the preparation of the chitosan nanoparticles (CS-NPs). The hydrodynamic diameter of the CS-MEO NPs was 130.7 nm, and the size of the CS-LEO NPs was 143.4 nm (as determined using Nanoparticle Tracking Analysis). The CS-NPs were incorporated into alginate hydrogels crosslinked with CaCl₂. The hydrogels showed significant water retention capacity (>80%) even after the swollen sample was kept in the aqueous HCl solution (pH 1.2) for 4 h, indicating a good stability of the network. The hydrogels were tested (a) for their ability to absorb dietary lipids and (b) for their antimicrobial activity against Gram-positive and Gram-negative foodborne pathogens. The antimicrobial activity of the hybrid hydrogels was comparable to that of the widely used food preservative sodium benzoate 5% w/v.

The anionic polymer sodium alginate, a linear copolymer of guluronic and mannuronic acids, is primarily present in brown algae. Copolymers are used in the sodium alginate preparation process to confer on the material strength and flexibility. Micelles and other polymeric nanoparticles are frequently made using the triblock copolymer Pluronic^® F-127. The purpose of the present study is to determine the effect of sodium alginate’s viscosity (low and medium) and the presence of Pluronic^® F-127 micelles on the swelling behavior of the prepared pure beads and those loaded with Pluronic^® F-127 micelles. The Pluronic^® F-127 nanomicelles have a size of 120 nm. The swelling studies were carried out at pH = 1.2 (simulated gastric fluid-SGF) for two hours and at pH = 6.8 (simulated intestinal fluid-SIF) for four more hours. The swelling of both low- and medium-viscosity alginate beads was minor at pH = 1.2, irrespective of the use of Pluronic^® F-127 nanomicelles. At pH = 6.8, without Pluronic^® F-127, the beads showed an enhanced swelling ratio for the first four hours, which was even higher in the medium-viscosity alginate beads. With the addition of Pluronic^® F-127, the beads were dissolved in the first and second hour, in the case of the low- and medium-alginate’s viscosity, respectively. In other words, the behavior of the mixed hydrogels was the same during the swelling experiments. Therefore, the presence of Pluronic^® F-127 nanomicelles and medium-viscosity sodium alginate leads to a higher swelling ratio. A model drug, acetyl salicylic acid (ASA), was also encapsulated in the mixed beads and ASA’s release studies were performed. In conclusion, the prepared systems, which are well characterized, show potential as delivery platforms for the oral delivery of active pharmaceutical ingredients and biopharmaceuticals.