Supercapacitors have the characteristics of high power density, long cycle life, and fast charge and discharge rates, making them promising alternatives to traditional capacitors and batteries. The use of transition-metal compounds as electrode materials for supercapacitors has been a compelling research topic in recent years because their use can effectively enhance the electrical performance of supercapacitors. The current research on capacitor electrode materials can mainly be divided into the following three categories: carbon-based materials, metal oxides, and conductive polymers. Nickel hydroxide (Ni(OH)₂) is a potential electrode material for use in supercapacitors. Depending on the preparation conditions, two crystal phases of nickel hydroxide, α and β, can be produced. When compared to α-NiOH, the structure of β-Ni(OH)₂ does not experience ion intercalation. As a result, the carrier transmission rate of α-Ni(OH)₂ is slower, and its specific capacitance value is smaller. Its carrier transport rate can be improved by adding conductive materials, such as graphene. β-Ni(OH)₂ was chosen as an electrode material for a supercapacitor in this study. Homemade low-pressure chemical vapor deposition graphene (LPCVD-Graphene) conductive material was introduced to modify β-Ni(OH)₂ in order to increase its carrier transport rate. The LPCVD method was used to grow high-quality graphene films on three-dimensional (3D) nickel foam substrates. Then, a hydrothermal synthesis method was used to grow β-Ni(OH)₂ nanostructures on the 3D graphene/nickel foam substrate. In order to improve the electrical properties of the composite structure, a high-quality graphene layer was incorporated between the nickel hydroxide and the 3D nickel foam substrate. The effect of the conductive graphene layer on the growth of β-Ni(OH)₂, as well as its electrical properties and electrochemical performance, was studied. When this β-Ni(OH)₂/CVD-Graphene/3D-NF (nickel foam) material was used as the working electrodes of the supercapacitor under a current density of 1 A/g and 3 A/g, they exhibited a specific capacitance of 2015 F/g and 1218.9 F/g, respectively. This capacitance value is 2.62 times higher than that of the structure without modification with a graphene layer. The capacitance value remains at 99.2% even after 1000 consecutive charge and discharge cycles at a current density of 20 A/g. This value also improved compared to the structure without graphene layer modification (94.7%).

The demand for power storage devices with good quality, fast charging and high energy density is becoming more and more urgent in today’s electronic technology. For batteries and traditional capacitors, it is an insurmountable challenge to combine fast charging and discharging, large capacitance and long-life properties. The characteristics of supercapacitors can meet all the above requirements at the same time. In this study, a simple one-step hydrothermal method was successfully used to grow β-nickel hydroxide nanocone particles directly on the 3D foamed nickel substrate as a working electrode material for supercapacitors. After growing β-nickel hydroxide crystals on 3D foamed nickel substrate, by controlling the cooling rate, a well-crystalized β-nickel hydroxide with good capacitance characteristics can be obtained. Cyclic voltammetry (CV), galvanostatic charge–discharge (GCD) and electrochemical impedance spectroscopy (EIS) were used to analyze the capacitance characteristics of the β-nickel hydroxide electrode. The research results show that the specific capacitance value of the β-Ni(OH)₂/3D nickel foam electrode material prepared at the cooling rate of 10 °C/h can reach 539 F/g with the charge–discharge test at a current density of 3 A/g. After 1000 continuous charge and discharge cycles, the material still retains 94.1% of the specific capacitance value.