Gyeongju bentonite is a Ca-bentonite and a highly compacted buffer material primarily considered in Korea, as a part of an engineered barrier system (EBS) of high-level radioactive waste (HLW) repository. During the repository lifetime, the buffer material should guarantee the safe disposal of HLW against any external mechanical impact, including seismic activity. Therefore, the dynamic deformation properties of buffer material is crucial to validate its lifetime effectiveness and performance. Even though there are some researches to investigate the dynamic properties of the bentonite buffer, there has been no researches for the Korean bentonite buffer. For this reason, the paper aims to evaluate the dynamic properties at small-strain of Gyeongju bentonite and correlate the small-strain deformation properties with unconfined compressive strength using seismic and static laboratory tests. Three sets of compacted cylindrical bentonite specimens with varying dry densities (1.50 g/cm³ to 1.77 g/cm³) were produced using a cold isostatic pressing technique under three different pressing loads. Free-free resonant column (FFRC) tests and unconfined compressive (UC) tests were performed. The FFRC tests measured deformation properties at small strain, including unconstrained and constrained compression velocities, Young’s modulus (E_max), constrained modulus (M_ax), material damping ratio (D_min), and Poisson’s ratio. The UC tests evaluated the compressive strength and secant modulus (E₅₀) at large-strain. In this study, it was found that the deformation properties (E_max and M_max) and unconfined compressive strength increase with the increase in a design rage of dry density. Poisson’s ratio measured at constrained boundary yields relatively constant value close to 0.4 for specimens at a range of dry density higher than 1.5 g/cm³. In addition, it was found that the elastic moduli have an almost linear relationship with the unconfined compressive strength. Finally, empirical equations between elastic moduli and unconfined compressive strength for Gyeongju compacted bentonite are proposed for a Koeran design guideline.

In response to climate change, wood pellets have been increasingly utilized as a sustainable energy source. However, their growing utilization increases the production of wood pellet fly ash (WA) by-products, necessitating alternative recycling technologies due to a shortage of discharging landfills. Thus, this research seeks to utilize WA by developing a new sustainable construction material, called wood pellet fly ash blended binder (WABB), and to validate its stabilizing performance in natural soils, namely weathered granite soil (WS). WABB is made from 50% WA, 30% ground granulated blast-furnace slag (GGBS), and 20% cement by dry mass. WS was mixed with 5%, 15%, and 25% WABB and was tested for a series of unconfined compressive strength (q_u), pH, and suction tests at 3, 7, 14, and 28 days. For the microstructural analyses, XRD, SEM, and EDS were employed. As the WABB dosage rate increased, the average q_u increased by 1.88 to 11.77, which was higher than that of compacted WS without any binder. Newly cementitious minerals were also confirmed. These results suggest that the effects of the combined hydration mechanism of WABB are due to cement’s role in facilitating early strength development, GGBS’s latent hydraulic properties, and WA’s capacity to stimulate the alkaline components of WABB and soil grains. Thus, this research validates a new sustainable binder, WABB, as a potential alternative to conventional soil stabilizers.