This work was concerned with the fabrication of a porous hydrogel system suitable for medium to heavy-exudating wounds where traditional hydrogels cannot be used. The hydrogels were based on 2-acrylamido-2-methyl-1-propane sulfonic acid (AMPs). In order to produce the porous structure, additional components were added (acid, blowing agent, foam stabilizer). Manuka honey (MH) was also incorporated at concentrations of 1 and 10% w/w. The hydrogel samples were characterized for morphology via scanning electron microscopy, mechanical rheology, swelling using a gravimetric method, surface absorption, and cell cytotoxicity. The results confirmed the formation of porous hydrogels (PH) with pore sizes ranging from ~50–110 µm. The swelling performance showed that the non-porous hydrogel (NPH) swelled to ~2000%, while PH weight increased ~5000%. Additionally, the use of a surface absorption technique showed that the PH absorbed 10 μL in <3000 ms, and NPH absorbed <1 μL over the same time. Incorporating MH the enhanced gel appearance and mechanical properties, including smaller pores and linear swelling. In summary, the PH produced in this study had excellent swelling performance with rapid absorption of surface liquid. Therefore, these materials have the potential to expand the applicability of hydrogels to a range of wound types, as they can both donate and absorb fluid.

Ternary-blended, melt-blown films of polylactide (PLA), polycaprolactone (PCL) and cellulose acetate butyrate (CAB) were prepared from preliminary miscibility data using a rapid screening method and optical ternary phase diagram (presented as clear, translucent, and opaque regions) as a guide for the composition selection. The compositions that provided optically clear regions were selected for melt blending. The ternary (PLA/PCL/CAB) blends were first melt-extruded and then melt-blown to form films and characterized for their tensile properties, tensile fractured-surface morphology, miscibility, crystallinity, molecular weight and chemical structure. The results showed that the tensile elongation at the break (%elongation) of the ternary-blended, melt-blown films (85/5/10, 75/10/15, 60/15/25 of PLA/PCL/CAB) was substantially higher (>350%) than pure PLA (ca. 20%). The range of compositions in which a significant increase in %elongation was observed at 55–85% w/w PLA, 5–20% w/w PCL and 10–25% w/w CAB. Films with high %elongation all showed good interfacial interactions between the dispersed phase (PCL and CAB) and matrix (PLA) in FE-SEM and showed improvements in miscibility (higher intermolecular interaction and mixing) and a decrease in the glass transition temperature, when compared to the low %elongation films. The decrease in M_w and M_n and the formation of the new NMR peaks (¹H NMR at 3.68–3.73 ppm and ¹³C NMR at 58.54 ppm) were observed in only the high %elongation films. These are expected to be in situ compatibilizers that are generated during the melt processing, mostly by chain scission. In addition, mathematical modelling was used to study the optimal ratio and cost-effectiveness of blends with optimised mechanical properties. These ternary-blended, melt-blown films have the potential for use in both packaging and medical devices with excellent mechanical performance as well as inherent economic and environmental capabilities.

Tailored porous structures of poly(2-hydroxyethyl methacrylate) (PHEMA) and silk sericin (SS) were used to create porous hydrogel scaffolds using two distinct crosslinking systems. These structures were designed to closely mimic the porous nature of the native extracellular matrix. Conventional free radical polymerization of 2-hydroxyethyl methacrylate (HEMA) was performed in the presence of different concentrations of SS (1.25, 2.50, 5.00% w/v) with two crosslinking systems. A chemical crosslinking system with N’N-methylene bisacrylamide (MBAAm) and a physical crosslinking system with dimethylurea (DMU) were used: C-PHEMA/SS (crosslinked using MBAAm) and C-PHEMA/pC-SS (crosslinked using MBAAm and DMU). The focus of this study was on investigating the impact of these crosslinking methods on various properties of the scaffolds, including pore size, pore characteristics, polymerization time, morphology, molecular interaction, in vitro degradation, thermal properties, and in vitro cytotoxicity. The various crosslinked networks were found to appreciably influence the properties of the scaffolds, especially the pore sizes, in which smaller sizes and higher numbers of pores with high regularity were seen in C-PHEMA/1.25 pC-SS (17 ± 2 μm) than in C-PHEMA/1.25 SS (34 ± 3 μm). Semi-interpenetrating networks were created by crosslinking PHEMA-MBAAm-PHEMA while incorporating free protein molecules of SS within the networks. The additional crosslinking step involving DMU occurred through hydrogen bonding of the -C=O and -N-H groups with the SS, resulting in the simultaneous incorporation of DMU and SS within the PHEMA networks. As a consequence of this process, the scaffold C-PHEMA/pC-SS exhibited smaller pore sizes compared to scaffolds without DMU crosslinking. Moreover, the incorporation of higher loadings of SS led to even smaller pore sizes. Additionally, the gelation time of C-PHEMA/pC-SS was delayed due to the presence of DMU in the crosslinking system. Both porous hydrogel scaffolds, C-PHEMA/pC-SS and PHEMA, were found to be non-cytotoxic to the normal human skin dermal fibroblast cell line (NHDF cells). This promising result indicates that these hydrogel scaffolds have potential for use in tissue engineering applications.

This study introduces biodegradable nursery bags using poly(lactic acid) (PLA), a widely used biodegradable polymer, and spent coffee grounds (SCGs), a byproduct of the brewing process in the coffee industry. SCGs were oil-extracted to produce extracted spent coffee grounds (exSCGs), which were characterized by their physical properties, chemical functionality, and thermal behavior. The exSCGs were blended with PLA at loadings of 5, 10, and 15 wt%. Analysis showed that exSCGs retained 3–5 wt% residual coffee oil, exhibiting a lower surface area (1.1163 m²/g) compared to SCGs (1.5010 m²/g), along with a higher pore volume (1.148 × 10⁻³ cm³/g) and pore size (~410 nm). All PLA/exSCG bio-composite films displayed a light brown color, well-dispersed exSCG particles, and excellent UV light barrier properties, with transmittance reduced to 1–2%. The residual coffee oil acted as a plasticizer, reducing the glass transition temperature, melting temperature, and crystallinity with increasing exSCG content. Mechanical testing revealed enhanced flexibility compared to neat PLA. Soil burial tests showed increased biodegradability with higher exSCG content, supported by SEM analysis revealing cracks around exSCG particles. The PLA/exSCG blend containing 10 wt% exSCGs exhibited optimal performance, with a significant increase in melt flow index (from 4.22 to 8.17 g/10 min) and approximately double the melt strength of neat PLA, balancing processability and mechanical properties. This innovation provides a sustainable alternative to plastic nursery bags, addressing waste valorization and promoting eco-friendly material development for agricultural applications.

Recently, there has been a growing concern among consumers regarding the safety of packaging products, particularly due to the presence of potentially harmful substances like synthetic pigments and inorganic dyes. These substances, which are often used to attract consumer attention, can migrate and contaminate products over extended shelf storage periods. To address this issue, the focus of this research was the development of a biodegradable packaging film using poly(butylene succinate) (PBS) incorporated with natural colorants extracted from roselle (RS) and sappan heartwood (SP). RS and SP serve as non-toxic and alternative pigments when compared to synthetic colorants. The biodegradable packaging films were prepared using blown film extrusion, encompassing different weight percentages of RS and SP (0.1%, 0.2%, and 0.3%). The films exhibited distinct colors, with RS films appearing pink to purple and SP films exhibiting an orange hue. The water vapor transmission rate slightly decreased with an increasing content of RS and SP extracts, indicating improved barrier properties. Additionally, the films showed reduced light transmittance, as evidenced by the UV–Vis light barrier results. The degree of crystallinity in the films was enhanced, as confirmed by X-ray diffraction and differential scanning calorimetry techniques. Regarding mechanical properties, the PBS/RS and PBS/SP films exhibited slight increases in tensile strength and elongation compared to neat PBS films. Moreover, the blended films demonstrated higher stability after undergoing an aging test, further highlighting their potential for use in biodegradable packaging applications. The key advantages of these films lie in their non-toxicity, biodegradability, and overall environmental friendliness.

This study investigated the performance of novel hydrogels based on poly (N-vinylformamide) (PNVF), copolymers of NVF with N-hydroxyethyl acrylamide (HEA) (P(NVF-co-HEA)), and 2-carboxyethyl acrylate (CEA) (P(NVF-co-CEA)), which were synthesized by photopolymerization using a UVLED light source. The hydrogels were analyzed for important properties such as equilibrium water content (%EWC), contact angle, freezing and non-freezing water, and diffusion-based in vitro release. The results showed that PNVF had an extremely high %EWC of 94.57%, while a decreasing NVF content in the copolymer hydrogels led to a decrease in water content with a linear relationship with HEA or CEA content. Water structuring in the hydrogels showed appreciably more variance, with ratios of free to bound water differing from 16.7:1 (NVF) to 1.3:1 (CEA), corresponding to PNVF having ~67 water molecules per repeat unit. The release studies of different dye molecules followed Higuchi’s model, with the amount of dye released from the hydrogels depending on the amount of free water and the structural interactions between the polymer and the molecule being released. The results suggest that PNVF copolymer hydrogels have potential for controlled drug delivery by altering the polymer composition to govern the amount and ratio of free to bound water contained in the hydrogels.