Healthcare-associated infections (HAIs) have a major impact on public health worldwide. Particularly, hospital surfaces contaminated with bacterial pathogens are often the origin of both sporadic cases and outbreaks of HAIs. It has been demonstrated that copper surfaces reduce the microbial burden of high touch surfaces in the hospital environment. Here we report the antimicrobial characterization of a novel composite coating with embedded copper particles, named Copper Armour™. The Copper Armour™ bactericidal activity was evaluated in in vitro assays against several bacterial pathogens, including Staphylococcus aureus, Pseudomonas aeruginosa, Escherichia coli O157:H7 and Listeria monocytogenes. Additionally, its antimicrobial properties were also evaluated in a pilot study over a nine-week period at an adult intensive care unit. For this, four high touch surfaces, including bed rails, overbed table, bedside table and IV Pole, were coated with Cooper Armour™, and its microbial burden was determined over a nine-week period. Copper Armour™ coated samples showed an in vitro reduction in bacterial burden of > 99.9% compared to control samples. Moreover, pilot study results indicate that Copper Armour™ significantly reduces the level of microbial contamination on high-touch surfaces in the hospital environment, as compared with standard surfaces. Based on its antimicrobial properties, Copper Armour™ is a novel self-sanitizing coating that exhibits bactericidal activity against important human pathogens and significantly reduces the microbial burden of hospital surfaces. This composite could be used as a self-sanitizing coating to complement infection control strategies in healthcare facilities.

Resistance to atmospheric corrosion in different environments located in Chile and the corrosion’s effect on the mechanical properties of SAE 1020 steel were studied. Atmospheric corrosivity categories at each station under study were determined. These categories were C2, for Laja; C3 and C4, for the Arica and Antarctic stations, respectively; and the most aggressive, C5 and higher at Quintero. These specific environments significantly influenced the mechanical responses of steel exposed for 36 months. Rupture elongation, the modulus of toughness, ultimate tensile strength, and hardness of the material all decreased as a function of environmental atmospheric aggressiveness. Lowered ductility is the result of the increased corrosion rate due to the high deposition of chlorides. This is due to the morphology of material degradation, which consequently occurs as pores, microstrains, and other defects that promote early rupture of the steel.

We studied atmospheric corrosion on Rapa Nui Island, using galvanized and non-galvanized SAE 1020 steel samples exposed on racks. We also added Charpy samples of both materials to directly determine the effect of corrosion rate on these materials' impact toughness. The results indicated a correlation between corrosion rate and toughness loss in the studied materials. In the corrosion study, we could also demonstrate the effect from increased insular population growth on contaminants which aid atmospheric corrosivity. Results showed that atmospheric SO₂ has tripled compared with similar corrosion studies done 20 years ago (Mapa Iberoamericano de Corrosión, MICAT), increasing corrosion rates. Our results show how human factors can influence changes in environmental variables that strengthen corrosion.

This study evaluated the behavior of three paint systems exposed to the Antarctic marine environment for 45 months compared to a control of uncoated carbon steel with a determined corrosion rate. At the study site, all environmental conditions, solar radiation, and the concentration of environmental pollutants (${\mathrm{Cl}}^{-}$ and SO₂) were evaluated. The paint systems differed in terms of the primer and top coat. Coated samples were studied before and after exposure. They were evaluated visually and using SEM to determine adhesion, abrasion, and contact angle; using the Evans X-Cut Tape Test; using ATR-FTIR spectroscopy to analyze the state of aging of the top layer; and using electrochemical impedance spectroscopy (EIS) for coat protection characterization. The corrosion rate obtained for steel was 85.64 µm year⁻¹, which aligned with a C5 environmental corrosivity category. In general, the evaluation in the period studied showed the paint systems had good adhesion and resistance to delamination, without the presence of surface rust, and exhibited some loss of brightness, an increase in the abrasion index, and a decrease in the percentage of reflectance due to aging. EIS showed good protection capability of the three coating schemes. In general, this type of paint system has not previously been evaluated in an extreme environment after 45 months of exposure to the environment. The results showed that the best behavior was found for the system whose top layer was acrylic–aliphatic polyurethane.