The introduction of a cellular structure in conductive polymer composites is supposed to be an effective way to ameliorate the electromagnetic interference (EMI) shielding properties.

The dispersion of carbon nanotubes (CNTs) is the bottleneck in CNT-reinforced metal matrix composites. In this work, CNT/Mg composites were prepared by grinding Mg powder and then dispersing CNTs via ball milling and hot pressing. The uniform distribution of Ni-coated CNTs in the matrix was achieved by optimizing the content of CNTs. Scanning electron microscope, high-resolution transmission electron microscopy and X-ray diffraction, optical microscopy, and compression tests were employed. With the CNT content being less than 1%, the CNTs can be evenly distributed in CNT/Mg composites, resulting in a sharp increase in strength. However, with the higher CNT content, the CNTs gradually cluster, leading decreased fracture strain and strength. Furthermore, the coated Ni in the CNTs reacts with the magnesium matrix and completely transforms into Mg₂Ni, significantly enhancing the interface bonding. This strong interface bonding and the diffusely distributed Mg₂Ni in the matrix significantly strengthen the CNT/Mg composite.

This study focused on the preparation of poly(ε-caprolactone)/carbon nanotubes (PCL/CNTs) composite membranes via electrospinning technology and investigated their performance in oil–water separation. The effects of varying CNTs contents and spinning parameters on the structure and properties of the membrane materials were systematically studied. A highly uniform diameter distribution of the PCL fiber was achieved by using the dichloromethane/dimethylformamide (DCM/DMF) composite solvent with volume ratio of 7:3, as well as a PCL concentration of ca. 17 wt.%. The optimal electrospinning parameters were identified as an applied voltage of 18 kV and a syringe pump flow rate of 1 mL·h⁻¹, which collectively ensured uniform fiber morphology under the specified processing conditions. The critical threshold concentration of CNTs in the composite system was determined to be 1 wt.%, above which the composite fibers exhibit a significant increase in diameter heterogeneity. Both pristine PCL fibrous membranes and PCL/CNTs composite membranes demonstrated excellent and stable oil–water separation performance, with separation efficiencies consistently around 90%. Notably, no significant attenuation in separation efficiency was observed after ten consecutive separation cycles. Furthermore, when incorporating 0.5 wt.% CNTs, the PCL/CNT composite membranes exhibited a 20% increase in separation flux for heavy oils compared to pristine PCL membranes. Additionally, CNTs, as a prototypical class of nanofillers for polymer matrix reinforcement, can potentially enhance the mechanical properties of composite films, thus effectively prolonging their service life.