This paper aims to evaluate the severities and causes of ground surface building and cropland damages after coal mining in a better way, and to clarify the correlation between the damage assessment indexes that influence mining. Against the backdrop of multi-seam mining in certain coal mines in China, the estimated results of each displacement and deformation were analyzed using GIS technology. The damage range determined for each deformation index is divided according to the displacement and deformation combined with the virtue of damage judgment threshold. The damage ranges on the ground surface based on the comprehensive value of each displacement and deformation index were obtained through superimposing those ranges delineated by each displacement and deformation index, and the law on influence from displacement indexes upon various levels of damage was analyzed in a quantitative manner accordingly. The results showed that coal mining destroyed 14 buildings and a cropland area of 11.96 hm²; among them, building damage was only associated with displacement indexes E (horizontal deformation) and T (inclined deformation). Seven buildings were solely destroyed by T alone; five buildings were solely damaged by E; two buildings were damaged jointly by E and T; and, moreover, with the aggravation in building damage level, the proportion of building damage due to E decreased while the proportion of building damage under the same level due to T increased. Regarding cropland destruction, the damage due to T accounted for 33.48% while the damage jointly caused by W (Subsidence), E and T accounted for 30.45%. Moreover, the proportion of damaged cropland area due to inclined deformation T was positively correlated with cropland damage level. These findings can provide a reference for rational judgment regarding civilian building and cropland destruction on the ground surface after coal mining.

Transmission towers located above mined-out areas may experience collapse or instability due to mining-induced ground subsidence and deformation, which poses significant risks to the safe operation of power transmission lines. To clearly evaluate the deformation resistance and failure threshold of transmission towers under mining-induced ground deformation, this article examines a typical 220 kV self-supporting transmission tower located in a mining area of Northern Shaanxi Province through a detailed three-dimensional finite element model constructed and simulated using ANSYS 2022. The mechanical response and failure process of the tower structure were systematically simulated under five typical deformation conditions: tilt, horizontal compression, horizontal tension, tilt–compression, and tilt–tension. The results indicate that under individual deformation conditions, the critical deformation values of the tower are 35 mm/m for tilt, 10 mm/m for horizontal compression, and 8 mm/m for horizontal tension, demonstrating that the structure is most sensitive to horizontal tensile deformation. Under combined deformation conditions, the critical deformation values for the combined tilt–compression and tilt–tension conditions exhibited a marked reduction, reaching 8 mm/m and 6 mm/m. Compared to individual deformation conditions, transmission towers demonstrate a significantly higher susceptibility to structural failure under combined deformation conditions. The displacement at the tower head and the tower tilt angle exhibit a linear positive correlation with the values of ground surface deformation. Under individual deformation conditions, the tilt of the tower was approximately 0.903 times the tilt deformation value and 0.089 times the values of horizontal compression and tension deformation, indicating that tilt deformation exerts a more pronounced influence on the inclination of the tower. Under combined deformation conditions, the tilt of the tower reached approximately 0.981 times that of the tilt–compression deformation value and 0.829 times that of the tilt–tension deformation value. Compared to the tower tilt induced individually by horizontal compression or tension deformation, the tilt under combined deformation conditions demonstrated a significantly greater value. Under mining-induced ground deformation, a redistribution of support reactions occurs, exhibiting either nonlinear or linear increasing trends depending on the type of deformation. The findings of this article provide a theoretical basis and data support for disaster prevention and control, safety evaluation, and structural design of transmission lines in mining areas.

In order to investigate the compression damage characteristics of the “interface section coal pillar–backfill body (ICPF)” composite structure formed after coal pillar excavation and gangue material backfill in the key technologies of coal pillar excavation and gangue material backfill replacement in the interface section of thick coal seams, an ICPF single-axis compression damage experiment under different internal dimensions of backfill was conducted using the PFC^2D numerical model, with the interface section coal pillar of a working face at a certain mine in northern Shaanxi Province as the research background. In addition, the stress–strain state, peak strength characteristics, damage mode, energy evolution, and damage characteristics of the ICPF composite were analyzed, and models for the evolution of the ICPF elastic modulus and compressive strength were established. The results showed that the stress–strain state of the ICPF changed from brittle to ductile as backfill strength decreased. The distribution of the elastic modulus is primarily influenced by backfill strength, and as the excavation–backfill width increases, the curve exhibits a distinct S-shaped distribution. The compressive strength decreases by up to 63.4% with an increase in excavation–backfill width and by up to 65.1% with a decrease in backfill strength. The sensitivity of compressive strength to backfill strength is greater than that to excavation–backfill width. Based on the established ICPF elastic modulus and compressive strength evolution model, the two mechanical properties were compared using model fitting, and the model fitting results were satisfactory. The ICPF exhibits three types of damage characteristics as the excavation and backfill width increases: oblique shear and tensile damage, edge coal stripping and X-shaped conjugate damage of the backfill body, and large-area plastic damage of the backfill body. By establishing a theoretical damage variable based on linear dissipation energy, damage factors can be quickly obtained from stress–strain curves. The damage curves all exhibit exponential growth, and their growth rates show certain dispersion as the excavation and backfill width increases and backfill strength decreases. Based on the brittleness index analysis of the ICPF composite, as the backfill strength decreases and excavation and backfill width increases, the brittleness index of the composite increases, and the tendency for impact increases. At an excavation and backfill width of 80 mm, rib damage tends to happen.

Due to the tendency of backfill slurry to stagnate within pipelines during transportation, a time-dependent rheological model for basalt fiber-reinforced gangue cemented slurry was developed based on the H-B rheological model and flocculation structure theory to ensure unimpeded slurry flow within pipelines over specified time periods. Experiments were conducted to investigate the time-dependent yield stress evolution of 9 mm fiber-reinforced gangue cemented slurry over time under varying conditions, specifically examining the effects of adding 9 mm fiber-reinforced (accounting for 0.5% of the total mass of the slurry) gangue cemented slurry under varying conditions. Significant effects of mass concentration, sucrose admixture content, and fly ash concentration on the yield stress of the slurry under different standing times were investigated. Research findings indicate that the yield stress of the paste increases with rising mass concentration and also rises with extended standing time. For slurries with mass concentrations ranging from 76% to 82%, the yield stress after 120 min of standing increased by 81.03%, 80%, 82%, and 97.48%, respectively, compared to freshly mixed slurries. The yield stress decreases with increasing sucrose dosage. Below 0.5% sucrose dosage, the rate of yield stress increase with standing time is relatively slow; above 0.5%, the rate increases more rapidly. After 120 min of standing, the yield stress of slurries with a sucrose dosage ranging from 0.25% to 1.00% increased by 48.66%, 54.42%, 32.90%, and 33.70%, respectively, compared to freshly mixed slurry. Yield stress decreased with increasing fly ash content and exhibited an overall steady upward trend with standing time. Based on the fitting surfaces depicting the variation in yield stress in filling materials over time under different influencing factors, fitting expressions were derived. Analysis of variance revealed that the time-dependent behavior of filling materials is primarily influenced by mass concentration, followed by retarder dosage and fly ash proportion.