This paper is a comprehensive experimental report on the neutron radiation effects of distributed optical fiber sensors with enhanced Rayleigh scattering profiles in an in-pile environment. Femtosecond laser direct writing was used to inscribe Type-II modifications in standard telecom fibers and radiation-hardened fibers with fluorine-doped cores. Rayleigh backscattering signals were enhanced for continuous 1.5 m. In-pile lead-out sensors tests were carried out at the MIT Research Reactor for two months, which was operated at a nominal power of 5.7 MW with fast neutron (>0.1 MeV) flux of 1.29 × 10 ¹⁴ n/cm ² /s and an in-core temperature of up to 560 °C. Using the Optical Frequency Domain Reflectometry technique, the backscattering profiles of fiber sensors were interrogated with a 3-cm spatial resolution to monitor the temperature profile of the reactor. Results show that laser inscribed Type-II modifications in the form of nanogratings are highly stable against extreme temperature and ionizing radiation. Both standard telecom fibers and radiation-hardened fibers with laser-enhanced Rayleigh profiles can continuously perform distributed temperature measurements over the entire duration of the in-pile testing. Temperature coefficients of sensors and spectral shift quality were studied as functions of total radiation fluence. To the best of our knowledge, we present for the first time, the temperature profile of an operating nuclear reactor core with 3-cm spatial resolution, enabled by distributed fiber sensors with laser-enhanced Rayleigh scattering profiles. The high spatial resolution measurements can provide valuable data for the design and validation of digital twin and virtual reality of nuclear energy systems.

We present a measurement of the rate of correlated neutron captures in the WATCHBOY detector, deployed at a depth of approximately 390 meters water equivalent (m.w.e.) in the Kimballton Underground Research Facility (KURF). WATCHBOY consists of a cylindrical 2 ton water target doped with 0.1% gadolinium, surrounded by a 40 ton undoped water hermetic shield. We present a comparison of our results with the expected rate of correlated neutron captures arising from high-energy neutrons incident on the outside of the WATCHBOY shield, predicted by a hybrid fluka-geant4-based simulation. The incident neutron energy distribution used in the simulation was measured by a fast neutron spectrometer, the 1.8 ton Multiplicity and Recoil Spectrometer (MARS) detector, at the same depth. We find that the measured detection rate of two correlated neutrons is consistent with that predicted by simulation. The result lends additional confidence in the detection technique used by MARS, and therefore in the MARS spectra as measured at three different depths. Confirmation of the fast neutron flux and spectrum is important as it helps validate the scaling models used to predict the fast neutron fluxes at different overburdens.

Optical frequency domain reflectometry measurements in internally clad single crystal sapphire fiber have received attention in recent years due to their high temperature distributed sensing potential. As work with these fibers has proceeded, there have been some inconsistencies in the results. Deeper investigation and testing has identified two critical considerations for the proper functioning of these fibers. First, users must address the propagation of multimode light along the outer surface of the fiber. By observing the far-field image of an internally clad sapphire fiber when adding index matching fluid to the outer fiber surface, we demonstrate the effects of removing the higher order modes from these fibers. The addition of index matching fluid resulted in nearly single mode performance where multimode performance was previously observed. Second, users must address the effect that coupling the fiber to the interrogator via silica based fiber has on the internally clad sapphire fiber's performance. Direct fusion splicing of silica to sapphire, as has been used in the recent work with these fibers, has a mode filtering effect which can be beneficial towards the modal behavior of the fibers. However, in this paper we demonstrate that the splicing can cause a sensing failure due to little or no low order mode light, that is useful for sensing, returning to the detector. The positive results from recent years have demonstrated that optical frequency domain reflectometry sensing performance will be successful in clad sapphire fiber; but only when the considerations described herein are addressed properly.

This research article explores the potential of optical fibers as sensors, highlighting their ability to measure various parameters such as temperature, pressure, stress, and radiation dose. The study focuses on investigating the material compatibility of optical fibers in challenging sensing environments like Gen II/II+ and advance nuclear reactors, as well as concentrated solar power (CSP) plants. Material compatibility tests were conducted to determine the feasibility of using fluorine and germanium optical fiber sensors in these environments. The study found that raw fibers were corrosion-resistant to lead bismuth eutectic at 600 °C, regardless of the coating. In molten salt environments, raw fibers were incompatible with FLiNaK but showed corrosion resistance to MgCl₂-NaCl-KCl. However, the survivability of raw fiber optics improved with a gold coating in FLiNaK. Raw fiber optics were found to be incompatible in high-temperature steam at 1200 °C and in a pressurized water reactor (PWR) at 300 °C.

This paper reports on laser fabrication, in-pile testing, and artificial intelligence (AI) enabled data analytics of distributed fiber sensors to monitor nuclear power systems (NPS). As intense radiation, high temperature, and hysteresis induce complex and significant sensor drifts, this paper studies long short-term memory (LSTM) neural network and k-nearest neighbor algorithm (k-NN) as data analytics tools to correct sensor drift. Using three thermocouples (TC) as calibration, LSTM neural networks were used to learn radiation effects exerted on fiber sensors located at the same location of TCs during normal states and simulated incidents of a test reactor. Fiber sensor measurements of other locations were rectified using k-NN based on knowledge harnessed by fiber sensors in calibration locations. The integrated sensor fusion and AI-enabled data analytics improved the temperature accuracy of fiber sensors to 2 °C during normal conditions. In a simulated reactor anomaly with a temperature excursion to 520 °C, the fiber sensors’ measurement accuracy was within 18 °C. This paper presents an integrated approach to fully harness the 1-cm-high spatial resolution measurement capabilities of distributed fiber sensors for nuclear energy applications. It can improve the applicability of fiber sensors as part of Instrumentation and Control (I&C) systems for future NPS.

High-temperature superconductor (HTS) magnet systems, especially those designed for fusion reactors, require effective and reliable monitoring to avoid damaging anomalies. In tokamaks, some of the magnetic coils are time-dependent, which causes strain and large inductive voltages within the magnet, rendering detection of incipient quench challenging. Ionizing radiation can also create material defects and lead to non-uniform degradation of conductors. The resulting decrease in critical current uniformity across the magnet, along with manufacturing defects, such as failure of structural materials or cooling systems, can all potentially initiate a quench. HTS magnets have a lower normal zone propagation velocity than low-temperature superconductors, and this causes normal zones to be localized, increasing the risk of permanent damage. Fiber optic sensors have several qualities that are essential in fusion systems. Unlike traditional voltage-based sensors, fiber optic cables are immune to the large electromagnetic fields present. This study presents and validates a fiber optic interrogation technique for monitoring magnetic confinement fusion and other high-temperature superconducting magnet systems. Coherent-phase optical time domain reflectometry (OTDR) allows for the high sampling rates (tens of kHz) necessary to quickly detect and mitigate quench events over the long distances required to monitor fusion magnet systems. This technique was demonstrated to successfully detect localized thermal transients at cryogenic temperatures as low as 6 K. These outcomes were also demonstrated using fibers embedded in HTS magnet coils at 77 K, verifying the potential for this interrogation technique’s use for failure detection in HTS coils.