Due to their versatile advantages, the use of additively manufactured components is growing. In addition, new additive manufacturing processes are constantly being developed, so that a wide range of printing processes are now available for metal. Despite the same starting material, the microstructure and thus also the final mechanical properties differ greatly compared to conventional processes. In most cases, only direction-dependent characteristic values from the uniaxial tension are used to qualify a printing process before it is used. The literature, on the other hand, demonstrates that the results are not transferable to other loading conditions. In this work, several engineering tests were integrated into a single test specimen so that they can be determined on the same specimen. The test specimen can be used to test tooth root strength, bending strength, notched bar impact energy, and thread strength depending on the mounting direction, thus representing industrial loading cases. In this study, test specimens were fabricated by conventional manufacturing (machining), L-PBF (Laser Powder Bed Fusion), and WA-DED (Wire Arc Direct Energy Deposition), and the results were compared using statistical methods. Factors to capture manufacturing influence and buildup direction were statistically validated on 316L. The work shows a benchmark with a typical initial microstructure of rolled and milled material, L-PBF, and WA-DED parts on loads close to the application and thus simplifies an industry-oriented evaluation of a new manufacturing process.

Within the scope of these investigations, the feasibility of a material bond between Ti-6Al-4V and the magnesium alloy AZ91 is analyzed. Ti-6Al-4V is frequently used for implants due to its biocompatibility, corrosion resistance, and specific strength. However, depending on the surface quality, the attachment behavior of the bone to the implant varies. Magnesium implants promote the regeneration of bone tissue and biodegrade as the bone tissue heals. Combining the properties of both materials in one implant enables a reduced implant volume and increased stability. For this reason, this study aims to demonstrate the feasibility of creating a material bond between the materials Ti-6Al-4V and AZ91. For this purpose, Ti-6Al-4V truncated cones and AZ91 sleeves were produced using the additive manufacturing process of laser powder bed fusion (L-PBF). The as-built sleeves were then pressed onto machined truncated cones. Since zinc serves as a lubricant and has good diffusion properties with the materials used as a result of heat treatment, a comparison was made between zinc-coated and the as-built Ti-6Al-4V samples. This showed that a bond was created after hot isostatic pressing and that the push-out force could be increased by more than 4.5 times. Consequently, a proof of feasibility was demonstrated, and a high potential for applications in medical technology was shown.

Modellierung von Einflüssen auf das Wire Arc Additive Manufacturing

Grüner et al.: Absicherung von Risiken beim Prozess des Wire Arc Additive Manufacturing. Industry 4.0 Science 1 2024, S. 63-69. Online: https://doi.org/10.30844/I4SD.24.1.63

Grüner et al.: Safeguarding Against Risks in the Wire Arc Additive Manufacturing Process. Industry 4.0 Science 1 2024, S. 63-69. Online: https://doi.org/10.30844/I4SE.24.1.63

Fischer et al.: Modeling Influences on the Wire Arc Additive Manufacturing Process. Industry 4.0 Science 1 2023, S. 80-87. Online: https://doi.org/10.30844/I4SE.23.80