Previous research has demonstred that microencapsulated phase change materials (MEPCMs) could significantly increase the energy storage density of solar thermal energy storage (TES) systems. Compared with traditional phase change materials (PCMs), MEPCMs have many advantages since they can limit their exposure to the surrounding environment, enlarge the heat transfer area, and maintain the volume as the phase change occurs. In this study, a new MEPCM for solar TES systems is developed by encapsulation of paraffin wax with poly (urea formaldehyde) (PUF). The experimental results revealed that agglomeration of MEPCM particles occurred during the encapsulation process which affected the uniformity of the particle size distribution profile when sodium dodecyl sulfate was used as an emulsifier. The differential scanning calorimetric (DSC) analysis results showed that the melting temperatures were slightly increased by 0.14–0.72 °C after encapsulation. A thermogravimetric (TG) test showed that the sample weight decreased while the weight loss starting temperature was slightly increased after encapsulation. Overall, the sample UF-2, fabricated with the binary emulsifiers of Brij 35 and Brij 30 and 5% nucleating agent, resulted in good particle dispersion and shell integrity, higher core material content and encapsulation efficiency, as well as improved thermal stability.

Phase change energy storage materials have been recognized as potential energy-saving materials for balancing cooling and heating demands in buildings. However, individual phase change materials (PCM) with single phase change temperature cannot be adapted to different temperature requirements. To this end, the concept of fabricating different kinds of microencapsulated PCM (MEPCM) and combing them to form a multiphase change material (MPCM) for multi-seasonal applications in buildings has been proposed. To prove the feasibility of this idea, three kinds of MEPCMs were fabricated and used for the development of three different composite MPCMs, classified as MPCM-1, MPCM-2, and MPCM-3. Analysis of the results shows that each MPCM sample was able to release latent heat at two different temperatures thus making them suitable for multi-temperature thermal energy storage applications. The phase change temperatures of the MPCMs were however found to be slightly reduced by 0.09–0.31 °C as compared with the MEPCMs samples. The measured energy storage capacities for the MPCMs were also reduced in the range of 6.3–11.4% as compared with the theoretical values but they displayed relatively good thermal stability behaviour of up to 197.8–218.8 °C. It was further identified that the phase change temperatures and latent heat of the MPCM was attributed to the weight percentages of individual components, as the theoretical values for the three MPCM samples were all in good accordance with the measured values. Therefore, optimizing the weight ratios of the MEPCM in MPCM samples and their corresponding thermophysical properties based on specific climatic conditions would be a necessary step to take in future investigations. Thermal performance enhancement of the MPCM is also being recommended as an essential part of further research.

A building-integrated photovoltaic-thermal (BIPVT) system integrates building envelope and photovoltaic-thermal collectors to produce electricity and heat. In this paper, the electrical and thermal performance of roof-based BIPVT systems developed in the recent two decades and their effects on heating and cooling load of the building are reviewed. According to the use of thermal energy from the photovoltaic (PV) panels, the roof-based BIPVT are classified into three classes: cooling of PV, air heating, and water heating. Each class is further divided into several types according to the designs of the integrated PV roofs. Compared with BIPV systems, the total efficiency of most BIPVT systems is significantly improved. However, the decrease in electricity output and adverse impact on the indoor environment is also found for some designs of BIPVT systems in some climates. The advantages and disadvantages of various designs are discussed. Issues to be further studied in the future are also provided in this review.