Passivating traps in perovskites: Low-temperature processing of planar organic-inorganic perovskite solar cells made through solution processing would allow for simpler manufacturing and the use of flexible substrates. However, materials currently in use form interfaces with charge carrier trap states that limit performance. Tan et al. used chlorine-capped TiO ₂ colloidal nanocrystal films as an electron-selective layer, which limited interface recombination in solution-processed solar cells. Such cells achieved certified efficiencies of 19.5% for active areas of 1.1 cm ² . Science , this issue p. 722

Solution-processed planar perovskite devices are highly desirable in a wide variety of optoelectronic applications; however, they are prone to hysteresis and current instabilities. Here we report the first perovskite–PCBM hybrid solid with significantly reduced hysteresis and recombination loss achieved in a single step. This new material displays an efficient electrically coupled microstructure: PCBM is homogeneously distributed throughout the film at perovskite grain boundaries. The PCBM passivates the key PbI₃⁻ antisite defects during the perovskite self-assembly, as revealed by theory and experiment. Photoluminescence transient spectroscopy proves that the PCBM phase promotes electron extraction. We showcase this mixed material in planar solar cells that feature low hysteresis and enhanced photovoltage. Using conductive AFM studies, we reveal the memristive properties of perovskite films. We close by positing that PCBM, by tying up both halide-rich antisites and unincorporated halides, reduces electric field-induced anion migration that may give rise to hysteresis and unstable diode behaviour.