A challenge that arises with periodontal regeneration surgery has been associated with the future development of periodontal regeneration membrane to prevent gingiva and fibroblasts invade the wound and allow alveolar bone successfully regenerated. Chitosan (CS) has the advantages of non-toxicity, biodegradation, biocompatibility, and has been widely used in wound dressings. A flexible film was made using polyvinyl alcohol (PVA) blending CS based thermosensitive hydrogel. The proposed 2% PVA/CS hydrogel has the highest swelling ratio about 720% after 60 min incubation and keeps its area after 10 min incubation for surgery suture. The elastic modulus of 0%, 1%, 2%, and 4% PVA/CS hydrogel were 7.75 ± 1.96, 0.91 ± 0.16, 0.75 ± 0.21, and 0.37 ± 0.06 MPa, respectively. The maximum strain of 2% PVA/CS hydrogel was 101.00 ± 28.03 (%). After 8 weeks biodegradation, the remain weight of 2% PVA/CS hydrogel was 71.36 ± 0.79 (%). In vitro cytotoxicity tests were performed and demonstrated PVA/CS hydrogel significantly improving cell proliferation. This study realized a promising flexible film for periodontal regeneration membrane that can prevent the rapid growth of fibroblasts to invade the wound and be used for periodontal regeneration surgery.

The sand-blasting and acid etching (SLA) method can fabricate a rough topography for mechanical fixation and long-term stability of titanium implant, but can not achieve early bone healing. This study used two kinds of plasma treatments (Direct-Current and Radio-Frequency plasma) to modify the SLA-treated surface. The modification of plasma treatments creates respective power range and different content functional OH groups. The results show that the plasma treatments do not change the micron scale topography, and plasma-treated specimens presented super hydrophilicity. The X-ray photoelectron spectroscopy (XPS)-examined result showed that the functional OH content of the RF plasma-treated group was higher than the control (SLA) and DC treatment groups. The biological responses (protein adsorption, cell attachment, cell proliferation, and differentiation) promoted after plasma treatments, and the cell responses, have correlated to the total content of amphoteric OH groups. The experimental results indicated that plasma treatments can create functional OH groups on SLA-treated specimens, and the RF plasma-treated SLA implant thus has potential for achievement of bone healing in early stage of implantation.

Poly(dopamine) films facilitate the initial attachment and proliferation of cells. Cell differentiation is enhanced by the release of strontium from the coatings.