In this study, two types of composites, polybutylene terephthalate (PBT) and epoxy resin (ER), reinforced with 20% of glass fiber (GF) are used as the comparative research objects. Their mechanical properties after thermal aging at 85~145 °C are evaluated by tensile strength and fracture morphology analysis. The results show that the composites have similar aging laws. The tensile strength of GF/PBT and GF/ER decrease gradually with the increase of aging temperature, while their elastic moduli are independent of the thermal treatment temperature. Scanning electron microscopy study of the fracture surface shows that separation of glass fiber from PBT and ER matrix becomes more obvious at higher aging temperature. The fibers on the matrix surface appear clear and smooth, and the whole pulled out GFs can be observed. As a main mechanical strength degradation mechanism, the deterioration of interface adhesion between the matrix and GF is discussed. A large difference in coefficients of thermal expansion of the matrix and GF is a main factor of the mechanical degradation.