Changes in the structural and textural properties of NiAl-layered double hydroxides (LDHs) (with 2–4 molar ratios of metals) and state of nickel that occur in different steps of the synthesis of nickel catalysts were studied using XRD, thermal analysis, TPR, low-temperature nitrogen adsorption, XANES, EXAFS, and electron microscopy methods. Relations between nickel content, catalyst reduction conditions, state of nickel, and its catalytic properties were revealed. It was shown that the use of NiAl LDH as the catalyst precursor even at a high content of active metal allows for the obtaining of the dispersed particles of supported nickel that are active in the aqueous-phase hydrogenation of furfural. The catalyst activity and conversion of furfural were found to increase with elevation of the catalyst reduction temperature and the corresponding growth of the fraction of reduced nickel. However, a lower reduction temperature (500 °C) makes it possible to form smaller nickel particles with the size of 4–6 nm, and a high Ni content (Ni:Al = 4) can be used to obtain the active Ni@NiAlO_x catalyst. Under mild reaction conditions (90 °C, 2.0 MPa), the furfural conversion reached 93%, and furfuryl alcohol was formed with the selectivity of 70%. Under more severe reaction conditions (150 °C, 3.0 MPa), complete conversion of furfural was achieved, and cyclopentanol and tetrahydrofurfuryl alcohol were the main hydrogenation products.

New coordination compounds of copper(II) with 2,5-bis(ethylthio)-1,3,4-thiadiazole (L¹) and 2,5-bis(pyridylmethylthio)-1,3,4-thiadiazole (L²) with compositions Cu(L¹)₂Br₂, Cu(L¹)(C₂N₃)₂, Cu(L²)Cl₂, and Cu(L²)Br₂ were prepared. The complexes were identified and studied by CHN analysis, infrared (IR) spectroscopy, powder X-Ray diffraction (XRD), and static magnetic susceptibility. The crystal structures of Cu(II) complexes with L¹ were determined. The structures of the coordination core of complexes Cu(L²)Cl₂ and Cu(L²)Br₂ were determined by Extended X-ray absorption fine structure (EXAFS) spectroscopy. Magnetization measurements have revealed various magnetic states in the studied complexes, ranging from an almost ideal paramagnet in Cu(L¹)₂Br₂ to alternating-exchange antiferromagnetic chains in Cu(L¹)(C₂N₃)₂, where double dicyanamide bridges provide an unusually strong exchange interaction (J₁/k_B ≈ −23.5 K; J₂/k_B ≈ −20.2 K) between Cu(II) ions. The cytotoxic activity of copper(II) complexes with L² was estimated on the human cell lines of breast adenocarcinoma (MCF-7) and hepatocellular carcinoma (HepG2).

The comprehensive study of the lanthanide-doped solid solutions CuCr_0.99Ln_0.01S₂ (Ln = La…Lu) magnetic properties was carried out using static magnetochemistry and differential scanning calorimetry techniques. It was shown that magnetic properties of CuCr_0.99Ln_0.01S₂ are significantly affected by the magnetic properties of the lanthanide ion. The magnetic susceptibility and the effective magnetic moment were found to deviate from the Curie-Weiss law in the temperature 90 K below and 50 K above the order-disorder transition at 695 K. The observed behavior of the temperature dependence of the effective magnetic moment in the order-disorder transition temperature region was described as a result of copper atoms redistribution over different types of the crystallographic sites.

The electronic structure of Os_0.5Pt_0.5 bimetallic nanoalloys is studied by X-ray photoelectron spectroscopy and X-ray absorption spectroscopy. The electronic population on the atoms of these alloys is determined from the obtained experimental data. It is shown that the alloy formation is accompanied by electron transfer from Os atoms to Pt atoms, while the sign and magnitude of the chemical shift are largely determined by the Madelung potential. The shape of the XPS spectra of core lines and the valence band indicate that the local density of states increases on the Os atoms near the Fermi level. Prospects of using the nanoalloys in catalytic reactions are discussed by analyzing the valence d-band parameters.