Laser powder bed fusion (LBPF) is currently the most mature metal additive manufacturing (AM) technology. While it does not have the same flexibility as directed energy deposition techniques to produce compositional gradients, LPBF can still be used to generate bimetallic parts by depositing one metal on a build plate made of another. Here, we print combinations of Ti-6Al-4V with Ta and characterize defects that occur at the interface. We use thermodynamic modeling to explain the formation of keyhole porosity and solidification cracks when Ta is built on a Ti baseplate, and the lack of defects when the materials are reversed. By understanding the mechanisms that lead to defect formation, the methodology demonstrated here can be applied to other material systems to efficiently design bimetallic LPBF processes.