Renewable hydrogen production by aqueous phase reforming (APR) over Ni/Al-Ca catalysts was studied using pure or refined crude glycerol as feedstock. The APR was carried out in a fixed bed reactor at 238 °C, 37 absolute bar for 3 h, using a solution of 5 wt.% of glycerol, obtaining gas and liquid products. The catalysts were prepared by the co-precipitation method, calcined at different temperatures, and characterized before and after their use by several techniques (XRD, ICP-OES, H₂-TPR, NH₃-TPD, CO₂-TPD, FESEM, and N₂-physisorption). Increasing the calcination temperature and adding Ca decreased the surface area from 256 to 188 m²/g, and its value after the APR changed depending on the feedstock used. The properties of the acid and basic sites of the catalysts influenced the H₂ yield also depending on the feed used. The Ni crystallite was between 6 and 20 nm. In general, the incorporation of Ca into Ni-based catalysts and the increase of the calcination temperature improved H₂ production, obtaining 188 mg H₂/mol C fed during the APR of refined crude glycerol over Ni/AlCa-675 catalyst, which was calcined at 675 °C. This is a promising result from the point of view of enhancing the economic viability of biodiesel.

The present work studied the stability and reusability of Ni/Al-Fe catalyst in the aqueous phase hydrogenolysis of glycerol without external hydrogen addition. The catalyst based on 28 molar % of Ni with 3/1 molar ratio of Al/Fe was prepared through co-precipitation. This catalyst presented the best performance in our last study which compares several Ni/Al-Fe catalysts with different molar ratios of Al/Fe. To see the influence of the pressurized water on the physicochemical characteristics of Ni/Al-Fe catalyst, a test of up to 9 h has been carried out. Fresh and used catalysts were characterized by various techniques: X-ray Diffraction (XRD), N₂-physisorption, field emission scanning electron microscopy (FESEM) and STEM. Glycerol conversion and carbon yield to gases and liquids did not vary significantly when compared at 3 h and 9 h. Furthermore, the morphology of the catalyst remains stable after continuous recycling under severe hydrothermal conditions. The nickel rich phase of the catalyst, which was determined by XRD and scanning transmission electron microscopy (STEM) techniques, showed a stable size after 9 h under reaction.