Due to its excellent performance, aerogel is considered to be an especially promising new material. Cellulose is a renewable and biodegradable natural polymer. Aerogel prepared using cellulose has the renewability, biocompatibility, and biodegradability of cellulose, while also having other advantages, such as low density, high porosity, and a large specific surface area. Thus, it can be applied for many purposes in the areas of adsorption and oil/water separation, thermal insulation, and biomedical applications, as well as many other fields. There are three types of cellulose aerogels: natural cellulose aerogels (nanocellulose aerogels and bacterial cellulose aerogels), regenerated cellulose aerogels, and aerogels made from cellulose derivatives. In this paper, more than 200 articles were reviewed to summarize the properties of these three types of cellulose aerogels, as well as the technologies used in their preparation, such as the sol–gel process and gel drying. In addition, the applications of different types of cellulose aerogels were also introduced.

In this study, first, a green and efficient NaOH/urea aqueous solution system was used to dissolve cellulose. Second, the resulting solution was mixed with sodium montmorillonite. Third, a cellulose/montmorillonite aerogel with a three-dimensional porous structure was prepared via a sol-gel process, solvent exchange and freeze-drying. The viscoelastic analysis results showed that the addition of montmorillonite accelerated the sol-gel process in the cellulose solution. During this process, montmorillonite adhered to the cellulose substrate surface via hydrogen bonding and then became embedded in the pore structure of the cellulose aerogel. As a result, the pore diameter of the aerogel decreased and the specific surface area of the aerogel increased. Furthermore, the addition of montmorillonite increased the compressive modulus and density of the cellulose aerogel and reduced volume shrinkage during the preparation process. In addition, the oil/water adsorption capacities of cellulose aerogels and cellulose/montmorillon aerogels were investigated.

In this study, composite aerogels with excellent mechanical properties were prepared by using carboxymethyl cellulose (CMC) as raw materials, with carboxylic carbon nanotubes (CNTs) as reinforcement. By controlling the mass fraction of CNTs, composite aerogels with different CNTs were prepared, and the surface morphology, specific surface area, compressive modulus, density and adsorption capacities towards different oils were studied. Compared to the pure CMC aerogel, the specific surface areas of CMC/CNTs were decreased because of the agglomeration of CNTs. However, the densities of composite aerogels were lower than pure CMC aerogel. This is because the CNTs were first dispersed in water and then added to CMC solution. The results indicated that it was easy for the low CMC initial concentration to be converted to low density aerogel. The compressive modulus was increased from 0.3 MPa of pure CMC aerogel to 0.5 MPa of 5 wt % CMC/CNTs aerogel. Meanwhile, the prepared aerogels showed promising properties as the adsorption materials. Because of the high viscosity, liquid possesses strong adhesion to the pore wall, the adsorption capacity of the CMC aerogel to the liquid increases as the viscosity of the liquid increases.