The beam-only connected reinforced concrete shear wall (BRW) is used as a reinforcing component to enhance the seismic performance of concrete-filled, double-skin steel tube (CFDST) frames. The effects of the BRW on seismic risks of CFDST frames are investigated. Three performance levels of limit states are defined and described according to the typical failure of test specimens and the existing definition of current guidance. A simplified numerical model is calibrated for CFDST frame-BRW structures, and test results validate it. Nonlinear dynamic analyses on a nine-story CFDST-BRW building are performed to investigate the effects of BRW on reducing the seismic risk of CFDST buildings. The results show that the BRW reduces the probability of collapse of the CFDST frame to 2.76% in 50 years, which can effectively reduce the probability of different degrees of damage in the service cycle of the structure. The results provide information for risk-informed decision-making on the design of CFDST frame-BRW structures.

To overcome brittle failure in conventional cold-formed steel–concrete (CFS-C) corner columns, this paper used fiber-reinforced concrete to replace ordinary concrete, investigating failure mechanisms and performance through systematic numerical simulations. A finite element model (FEM) was established and validated by experiments, and the errors for ultimate capacity were within 10%. A series of numerical models was established for parametric analyses focusing on the effects of the parameters of polypropylene fiber (PF), carbon fiber (CF), steel fiber (SF), and bamboo fiber (BF) with different volume dosages and the thickness of cold-formed steel (CFS) on the axial compression ultimate capacity and corresponding displacement of CFS composite corner columns. The results indicated that (1) PF effectiveness was dependent on steel thickness: thicker steel suppressed micro-defects, activated the toughening potential of PF, and increased the ultimate capacity of the columns by 24.8%. (2) CF had a critical dosage of 0.4%: at this dosage, CF increased the column’s ultimate capacity by 14.1% through stress redistribution, while when the dosage exceeded this value, fiber agglomeration caused a reduction in the column’s strength, with a maximum decrease of 16.2%. (3) SF effectiveness showed a linear increase: at a dosage of 1.6%, SF formed a synergistic three-dimensional bridging network and generated a confinement effect, increasing the column’s ultimate capacity by 36.5% and displacement by 92.2%. (4) BF mainly improved the ductility of columns: through crack bridging and pull-out energy dissipation, BF increased column displacement by 33.2%. (5) The modified Eurocode 4 formula could reduce the calculation error of ultimate capacity from 6.3% to within 1%. The findings guide optimal fiber selection and dosage in practice, promoting such columns’ use in seismic and load-bearing structures.