European paper mills are currently facing the question of whether recovered paper, their main raw material, will be available in sufficient quantities and an acceptable quality in the future. An alternative to recovered paper or wood fiber is the use of agricultural residues such as wheat straw. Sodium carbonate-based straw pulping processes have the advantage of not requiring recausticizing for chemical recovery, which reduces investment and operating costs. With the addition of oxygen, delignification can be significantly improved to provide pulps suitable for bleaching. This study compares the pulping of wheat straw using sodium carbonate, sodium carbonate + oxygen, and sodium carbonate + sodium hydroxide + oxygen. Pulping parameters such as temperature, retention time, and chemical charge were varied, and their influence on pulp properties was studied. The use of sodium carbonate alone produced pulps with high yields of up to 72% and comparably high burst and compressive strength. The addition of oxygen and small amounts of sodium hydroxide produced pulps with a high initial brightness of 42 %ISO and a low kappa number (18), still at high pulp yields of 62%. These pulps were two-stage bleached to achieve brightness levels of up to 73 %ISO.

This paper evaluates the modification of fiber morphology and the strength property development of paper from Enset fiber as a function of soda pulping conditions and refining energy. Soda pulping was conducted at pulping temperatures between 160 and 180 °C. The NaOH charge was 16, 20, and 24% based on the initial raw material. The beating of pulp was conducted using a Jokro mill. The refining of pulp was conducted in a laboratory refiner at different refining intensities. The mild Jokro mill beating was not effective on Enset fiber pulp. On the other hand, the laboratory refiner effectively refined the pulp. The fiber morphology was altered in the way of improving the paper formation and strength. The beating degree of the pulp was increased to about 49 °SR. The tensile index was enhanced to around 80 Nm/g using a refining energy input of 250 kwh/t. From the results, it can be concluded that Enset fiber pulp is suitable for packaging papers due to its high strength level. On the other hand, Enset fiber can be a potential raw material for specialty papers like filter paper and tea bags because of its high porosity.