Chromium and silicon are often introduced to increase the performance of TiAlN hard coatings in dry tribological contacts. The addition of Cr and Si during a high-power impulse magnetron sputtering (HiPIMS) deposition process leads to high-quality TiAlCrSiN films. In this paper, the analysis of friction and wear of these films is conducted by oscillation tribometry under dry conditions with a subsequent mapping of the surface topography. Both abrasion- and adhesion-dominated conditions are realized using different steel counter bodies. Oscillation-frequency-dependent experiments show a significant impact of the compositional variation on friction and wear. It is shown that the TiAlCrSiN coating investigated has a higher coefficient of friction and a lower wear resistance compared to counterparts made of 100Cr6. The friction coefficient could be reduced by using a V2A counterpart. The results can be understood in terms of a reduced adhesion of both oxidic and metallic wear debris at the TiAlCrSiN surface. The study provides valuable progress towards the development of advanced cutting tools, e.g., for stainless steel.

The rheological and tribological properties of environmentally compatible lubricants of different bases (native oil, synthetic ester, polyalkylene glycol‐containing oil) compared to a conventional, mineral oil‐based lubricant are investigated in order to develop toxicologically harmless and technically suitable lubricants for electromechanical drives. The aging of the oil is also considered. The results of this study reveal that the properties of polyalkylene glycol‐containing and synthetic ester‐based lubricants have the potential to act as substitutes for lubricants containing mineral oil. By examining and improving the properties of sustainable lubricants, gear oils that are partially or totally non‐mineral oil based will be highly attractive in the future.