In this work, we use a two-step metal-assisted chemical etching method to produce films of silicon nanowires shaped in micrograins from metallurgical-grade polycrystalline silicon powder. The first step is an electroless plating process where the powder was dipped for few minutes in an aqueous solution of silver nitrite and hydrofluoric acid to permit Ag plating of the Si micrograins. During the second step, corresponding to silicon dissolution, we add a small quantity of hydrogen peroxide to the plating solution and we leave the samples to be etched for three various duration (30, 60, and 90 min). We try elucidating the mechanisms leading to the formation of silver clusters and silicon nanowires obtained at the end of the silver plating step and the silver-assisted silicon dissolution step, respectively. Scanning electron microscopy (SEM) micrographs revealed that the processed Si micrograins were covered with densely packed films of self-organized silicon nanowires. Some of these nanowires stand vertically, and some others tilt to the silicon micrograin facets. The thickness of the nanowire films increases from 0.2 to 10 μm with increasing etching time. Based on SEM characterizations, laser scattering estimations, X-ray diffraction (XRD) patterns, and Raman spectroscopy, we present a correlative study dealing with the effect of the silver-assisted etching process on the morphological and structural properties of the processed silicon nanowire films.

Based on the widely used wet metal-assisted electroless etching, we develop in this work a novel vapor-phase silver-assisted chemical etching (VP-Ag-ACE) suitable for the elaboration of highly doped p-silicon (Si) nanostructures with strong, visible, and multi-peak photoluminescence (PL) emissions. The lateral and vertical etching rates (LER and VER) were discussed based on the etching mechanism of the VP-Ag-ACE. The antireflective suitability of the vapor-etched layer has been evaluated by a reflectivity measurement and exhibits reflectivity values lower than 3%. The PL emission at both room and low temperatures emissions were deeply discussed and correlated with the structural properties of the Si morphologies and their surface states based on the FTIR results.