NiAl-based intermetallic coatings were obtained using non-vacuum electron beam cladding on low-carbon steel. The structure of the coatings was investigated using optical microscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), electron backscatter diffraction (EBSD), and X-ray diffraction (XRD). The coatings mostly consisted of grains elongated perpendicular to the substrates, with a strong texture along the grain growth direction. The coatings contained about 14 at. % Fe, which appeared due to the partial melting of the steel substrate. At the bottom of the coatings, an inhomogeneous mixing zone with an increased concentration of Fe was formed; at the “substrate–coating” interface, a thick layer with a Fe50-Ni25-Al25 at. % composition was observed. The samples exhibited weight gains of 0.1, 0.8, 2.14, and 3.4 mg/cm² after 100 h of oxidation at 700, 800, 900, and 1000 °C, respectively. The oxide layer contained α-Al₂O₃ and θ-Al₂O₃, and the presence of iron atoms contributed to the formation of a small amount of spinel. During the oxidation process, a layer with a high Fe content (~60 at. %) formed along the boundary between the oxide film and the NiAl-based material, which had a positive effect on the formation of a non-porous “oxide–coating” interface.

In this study, Al₂₁Co₂₂Cr₂₂Fe₁₃Ni₂₂ high-entropy coatings were produced on steel substrates by non-vacuum electron beam cladding of Co, Cr, and NiAl powders. The high-temperature oxidation behavior of the coatings was studied by holding the specimens at 900 °C in air. The microstructure and phase constitution of the samples were studied both in the as-cladded state and after the heat treatment. The microstructure was characterized using light microscopy (LM) and scanning electron microscopy (SEM). Synchrotron X-ray diffraction (SXRD) and energy-dispersive X-ray spectroscopy (EDX) were used to study the phase constitution of the coatings and the “coating-substrate” interface. The coating consisted of disordered bcc (A2), ordered bcc (B2), and disordered fcc (A1) phases. Annealing the coatings for 50 h at 900 °C led to the formation of fcc precipitates in the bcc dendritic grains and a mixture of fcc and σ-phase particles in the interdendritic regions. Needle-like nanosized B2-precipitates were formed due to annealing in the fcc grains at the coating/substrate interface. The microhardness at the top of the as-cladded coating was 585 HV and gradually decreased towards the substrate. A more uniform distribution of the microhardness was obtained after the annealing. Its average value was 441 HV. Rhomboid Cr₂O₃, needle-like Al₂O₃, and spinels of a different morphology were found on the surface of the samples after oxidation at 900 °C.