Magnesium with its mechanical properties and nontoxicity is predetermined as a material for biomedical applications; however, its high reactivity is a limiting factor for its usage. Powder metallurgy is one of the promising methods for the enhancement of material mechanical properties and, due to the introduced plastic deformation, can also have a positive influence on corrosion resistance. Pure magnesium samples were prepared via powder metallurgy. Compacting pressures from 100 MPa to 500 MPa were used for samples’ preparation at room temperature and elevated temperatures. The microstructure of the obtained compacts was analyzed in terms of microscopy. The three-point bendisng test and microhardness testing were adopted to define the compacts’ mechanical properties, discussing the results with respect to fractographic analysis. Electrochemical corrosion properties analyzed with electrochemical impedance spectroscopy carried out in HBSS (Hank’s Balanced Salt Solution) and enriched HBSS were correlated with the metallographic analysis of the corrosion process. Cold compacted materials were very brittle with low strength (up to 50 MPa) and microhardness (up to 50 HV (load: 0.025 kg)) and degraded rapidly in both solutions. Hot pressed materials yielded much higher strength (up to 250 MPa) and microhardness (up to 65 HV (load: 0.025 kg)), and the electrochemical characteristics were significantly better when compared to the cold compacted samples. Temperatures of 300 °C and 400 °C and high compacting pressures from 300 MPa to 500 MPa had a positive influence on material bonding, mechanical and electrochemical properties. A compacting temperature of 500 °C had a detrimental effect on material compaction when using pressure above 200 MPa.

The main advantage of magnesium and its alloys is high specific strength and biocompatibility. A modern approach to magnesium-based materials preparation is powder metallurgy. This technique allows preparation of new materials with a unique structure, chemical composition, and controlled porosity. In this study, cold compaction of magnesium powder was studied. Magnesium powder of average particle size of 30 μm was compacted applying pressures of 100 MPa, 200 MPa, 300 MPa, 400 MPa and 500 MPa at laboratory temperature. Influence of compacting pressure was studied with microstructural and electrochemical corrosion characteristics analysis. The resulting microstructure was studied in terms of light and electron microscopy. Obtained electrochemical characteristics were compared with those of wrought magnesium. Compacting pressure had a significant influence on microstructure and electrochemical characteristics of prepared bulk magnesium. With the increase in compaction pressure, the porosity decreased. Compacting pressures of 300 MPa, 400 MPa and 500 MPa led to the similar microstructure of the prepared material. Polarization resistance of compacted magnesium was much lower and samples degraded faster when compared to wrought magnesium. Also, the corrosion degradation mechanism changed due to the microstructural differences between the material states.