BaMoO₄ was obtained via facile mechanochemical synthesis at room temperature and a solid-state reaction. An evaluation of the phase composition and structural and optical properties of BaMoO₄ was conducted. The influence of different milling speeds on the preparation of BaMoO₄ was explored. A shorter reaction time for the phase formation of BaMoO₄ was achieved using a milling speed of 850 rpm. A milling speed of 500 rpm led to partial amorphization of the initial reagents and to prolongation of the synthesis time of up to 3 h of milling time. Solid-state synthesis was performed via heat treatment at 900 °C for 15 h. X-ray diffraction analysis (XRD), infrared (IR) and UV diffuse reflectance (UV-Vis) and photoluminescence (PL) spectroscopy were carried out to characterize the samples. Independently of the method of preparation, the obtained samples had tetragonal symmetry. The average crystallite sizes of all samples, calculated using Scherrer’s formula, were in the range of 240 to 1540 Å. IR spectroscopy showed that more distorted structural MoO₄ units were formed when the compound was synthesized via a solid-state reaction. The optical band gap energy of the obtained materials was found to decrease from 4.50 to 4.30 eV with increasing crystallite sizes. Green- and blue-light emissions were observed for BaMoO₄ phases under excitation wavelengths of 330 and 488 nm. It was established that the intensity of the PL peaks depends on two factors: the symmetry of MoO₄ units and the crystallite sizes.

CaWO₄ nanoparticles were obtained by facile mechanochemical synthesis at room temperature, applying two different milling speeds. Additionally, a solid-state reaction was employed to assess the phase composition, structural, and optical characteristics of CaWO₄. The samples were analyzed by X-ray diffraction (XRD), transition electron microscopy (TEM), and Raman, infrared (IR), ultraviolet–visible (UV–Vis) reflectance, and photoluminescence (PL) spectroscopies. The phase formation of CaWO₄ was achieved after 1 and 5 h of applied milling speeds of 850 and 500 rpm, respectively. CaWO₄ was also obtained after heat treatment at 900 °C for 12 h. TEM and X-ray analyses were used to calculate the average crystallite and grain size. The Raman and infrared spectroscopies revealed the main vibrations of the WO₄ groups and indicated that more distorted structural units were formed when the compound was synthesized by the solid-state method. The calculated value of the optical band gap of CaWO₄ significantly increased from 2.67 eV to 4.53 eV at lower and higher milling speeds, respectively. The determined optical band gap of CaWO₄, prepared by a solid-state reaction, was 5.36 eV. Blue emission at 425 (422) nm was observed for all samples under an excitation wavelength of 230 nm. CaWO₄ synthesized by the solid-state method had the highest emission intensity. It was established that the intensity of the PL peak depended on two factors: the morphology of the particles and the crystallite sizes. The calculated color coordinates of the CaWO₄ samples were located in the blue region of the CIE diagram. This work demonstrates that materials with optical properties can be obtained simply and affordably using the mechanochemical method.

In this study, the effects of ball milling conditions on the phase formation, symmetry of structural units and photoluminescence features of SrMoO ₄ were investigated.

Nanocrystalline CoWO₄ sampled were synthesized using a simple mechanochemical approach and a solid-state reaction, respectively. The formation of nanocrystalline CoWO₄ was characterized by X-ray diffraction (XRD) and infrared spectroscopy (IR). The optical properties of the obtained samples were explored by diffuse reflectance UV–visible (DRS) and photoluminescence (PL) techniques. A milling speed of 850 rpm led to the direct synthesis of monoclinic CoWO₄ with a short reaction time (1 h). The complete reaction did not occur in the solid-state synthesis. The obtained samples had monoclinic crystal systems with different lattice parameters. The average crystallite sizes of CoWO₄ were in the range of 20 to 180 nm. The TEM investigation showed that the morphology of the CoWO₄ particles differed depending on the preparation conditions. The values of the determined optical bandgap of CoWO₄ were the range of 1.89 to 2.18 eV, according to diffusion reflectance spectroscopy in the ultraviolet-to-visible range. Broader blue–green emission spectra with peaks at 430 nm were observed for samples prepared via both routes. The CIE color coordinates of the CoWO₄ samples lay in the blue and purple regions. The quantum yields of the CoWO₄ samples synthesized after 1 h and 5 h milling times at 850 rom were 0.34 and 0.67%, respectively. This study proposes an affordable mechanochemical approach for blue–green phosphors that could possibly be used in various light-emitting diodes (LEDs).